The heat treatment microstructures and XRD patterns of the Mg-8Gd-5Y-2Zn-0.5Zr(wt.%) alloy in the absence and presence of a 10T high magnetic field have been investigated.The investigations show that the grains of α-...The heat treatment microstructures and XRD patterns of the Mg-8Gd-5Y-2Zn-0.5Zr(wt.%) alloy in the absence and presence of a 10T high magnetic field have been investigated.The investigations show that the grains of α-Mg demonstrate a preferred orientation due to the magnetic driving force.In addition,high magnetic fields can promote the growth of the long period ordered structure(LPS) phase to the grain interior.And the corresponding mechanisms are also discussed in this article.展开更多
In-situ TiB_2/AZ31 composites were prepared by utilizing the SHS reaction of Al-Ti-B system in the molten magnesium,and the effects of external physical fields on the dispersion of TiB_2 particles were investigated.Th...In-situ TiB_2/AZ31 composites were prepared by utilizing the SHS reaction of Al-Ti-B system in the molten magnesium,and the effects of external physical fields on the dispersion of TiB_2 particles were investigated.The results show that high-energy ultrasonic vibration could effectively break up the particle clusters and make the TiB2 particles uniformly distributed in the melt of TiB_2/AZ31 composites.The compound field(high-energy ultrasonic field coupling with electromagnetic field)could not only distribute the TiB_2 particles into the matrix uniformly,but also make the grains of α-Mg free and uniform further than the ultrasonic field solo.The average grain size of as-cast TiB_2/AZ31 composites was reduced from 173μm to 94μm.展开更多
基金Item Sponsored by the Fundamental Research Funds for the Central University[NO.DUT12JN02]
文摘The heat treatment microstructures and XRD patterns of the Mg-8Gd-5Y-2Zn-0.5Zr(wt.%) alloy in the absence and presence of a 10T high magnetic field have been investigated.The investigations show that the grains of α-Mg demonstrate a preferred orientation due to the magnetic driving force.In addition,high magnetic fields can promote the growth of the long period ordered structure(LPS) phase to the grain interior.And the corresponding mechanisms are also discussed in this article.
基金Item Sponsored by National High Technology Research and Development Program of China[No.2009AA03Z525]Aviation Science Foundation of China[No.20095263005]
文摘In-situ TiB_2/AZ31 composites were prepared by utilizing the SHS reaction of Al-Ti-B system in the molten magnesium,and the effects of external physical fields on the dispersion of TiB_2 particles were investigated.The results show that high-energy ultrasonic vibration could effectively break up the particle clusters and make the TiB2 particles uniformly distributed in the melt of TiB_2/AZ31 composites.The compound field(high-energy ultrasonic field coupling with electromagnetic field)could not only distribute the TiB_2 particles into the matrix uniformly,but also make the grains of α-Mg free and uniform further than the ultrasonic field solo.The average grain size of as-cast TiB_2/AZ31 composites was reduced from 173μm to 94μm.