Al_(2)O_(3)-SiC castables,for the relining of BF hearths in mid-campaign repair,were sampled and investigated after two years’service.The chemical and mineralogical characteristics of the residual castables were anal...Al_(2)O_(3)-SiC castables,for the relining of BF hearths in mid-campaign repair,were sampled and investigated after two years’service.The chemical and mineralogical characteristics of the residual castables were analyzed by X-ray diffraction,scanning electron microscopy,and energy dispersive X-ray spectrometry to study the erosion mechanism.The results show that as gaseous K diffuses in the castables,leucite(KAlSi_(2)O_(8))and multiple cracks are formed.Molten iron and slag penetrate through the cracks to form anorthite([Ca,Na][Al,Si]_(4)O_(8))and iron,which will not form an embrittlement layer similar to carbon bricks.The entire repair of the hearth with Al_(2)O_(3)-SiC castables combined with the design of thin-wall lining hearth eliminates“elephant foot shaped”erosion,greatly prolonging the service life of the hearth lining.展开更多
文摘Al_(2)O_(3)-SiC castables,for the relining of BF hearths in mid-campaign repair,were sampled and investigated after two years’service.The chemical and mineralogical characteristics of the residual castables were analyzed by X-ray diffraction,scanning electron microscopy,and energy dispersive X-ray spectrometry to study the erosion mechanism.The results show that as gaseous K diffuses in the castables,leucite(KAlSi_(2)O_(8))and multiple cracks are formed.Molten iron and slag penetrate through the cracks to form anorthite([Ca,Na][Al,Si]_(4)O_(8))and iron,which will not form an embrittlement layer similar to carbon bricks.The entire repair of the hearth with Al_(2)O_(3)-SiC castables combined with the design of thin-wall lining hearth eliminates“elephant foot shaped”erosion,greatly prolonging the service life of the hearth lining.