Cu^(+)-doped alkali borosilicate glasses with different Na_(2)O contents were prepared by the melting method,and the effects of different R values(R=Na_(2)O/B_(2)O_(3))on the structure,ion presence state and luminesce...Cu^(+)-doped alkali borosilicate glasses with different Na_(2)O contents were prepared by the melting method,and the effects of different R values(R=Na_(2)O/B_(2)O_(3))on the structure,ion presence state and luminescence properties of Cu^(+)-doped alkali borosilicate glasses were investigated.The analysis by FT-IR and Raman spectroscopy shows that,with the increase of R value of the glass,the[BO_(3)]in the structure of Cu^(+)-doped alkali borosilicate glass transforms into[BO_(4)]and the number of non-bridging oxygen in the glass network appears to be slightly increased.The absorption spectra and EPR analysis reveal that the Cu^(+)content in the glass gradually decreases and the Cu^(2+)content gradually increases as the R value of the glass increases.XPS and PL tests further indicate that the transformation of the octahedral coordination structure of Cu^(+)to the octahedral coordination structure of Cu^(2+)and the cubic coordination structure of Cu^(+)occurs in the glass as the R value of the glass increases.This transformation can effectively reduce the concentration quenching phenomenon of Cu^(+)and improve the fluorescence luminescence intensity of the glass samples.Meanwhile,the samples were found to have luminescence tunability as well as good thermal stability.展开更多
基金Funded by the Key R&D Projects in Hubei Province of China(No:2020BAB061)。
文摘Cu^(+)-doped alkali borosilicate glasses with different Na_(2)O contents were prepared by the melting method,and the effects of different R values(R=Na_(2)O/B_(2)O_(3))on the structure,ion presence state and luminescence properties of Cu^(+)-doped alkali borosilicate glasses were investigated.The analysis by FT-IR and Raman spectroscopy shows that,with the increase of R value of the glass,the[BO_(3)]in the structure of Cu^(+)-doped alkali borosilicate glass transforms into[BO_(4)]and the number of non-bridging oxygen in the glass network appears to be slightly increased.The absorption spectra and EPR analysis reveal that the Cu^(+)content in the glass gradually decreases and the Cu^(2+)content gradually increases as the R value of the glass increases.XPS and PL tests further indicate that the transformation of the octahedral coordination structure of Cu^(+)to the octahedral coordination structure of Cu^(2+)and the cubic coordination structure of Cu^(+)occurs in the glass as the R value of the glass increases.This transformation can effectively reduce the concentration quenching phenomenon of Cu^(+)and improve the fluorescence luminescence intensity of the glass samples.Meanwhile,the samples were found to have luminescence tunability as well as good thermal stability.