(ZrMg)xY2-2xMo3O12(x=0.0,0.1,0.2,0.3,0.4,0.5,0.6,0.7,0.8,0.9,and 1)ceramics have been synthesized to obtain less hygroscopicity and negative thermal expansion.With increasing the substitution of(ZrMg)^6+(ion radius 7....(ZrMg)xY2-2xMo3O12(x=0.0,0.1,0.2,0.3,0.4,0.5,0.6,0.7,0.8,0.9,and 1)ceramics have been synthesized to obtain less hygroscopicity and negative thermal expansion.With increasing the substitution of(ZrMg)^6+(ion radius 7.2×10^-11 m)for Y3+(ion radius 9×10^-11 m),the crystal water are reduced obviously.The linear thermal expansion coefficient is improved with increasing the content of(ZrMg)^6+.The material shows near zero thermal expansion(-0.12×10^-6 K^-1,430-870 K)with x=0.7.Meanwhile,ZrMgMo3O12 shows low non-hygroscopicity and negative thermal expansion,but low softening temperature.After substituting amount of Y^3+for(ZrMg)^6+in ZrMgMo3O12(x=0.8),the softening temperature increases remarkably(750 K to 830 K)and it presents near zero thermal expansion.展开更多
基金Funded by National Natural Science Foundation of China(Nos.61704156,11847099 and 10974183).
文摘(ZrMg)xY2-2xMo3O12(x=0.0,0.1,0.2,0.3,0.4,0.5,0.6,0.7,0.8,0.9,and 1)ceramics have been synthesized to obtain less hygroscopicity and negative thermal expansion.With increasing the substitution of(ZrMg)^6+(ion radius 7.2×10^-11 m)for Y3+(ion radius 9×10^-11 m),the crystal water are reduced obviously.The linear thermal expansion coefficient is improved with increasing the content of(ZrMg)^6+.The material shows near zero thermal expansion(-0.12×10^-6 K^-1,430-870 K)with x=0.7.Meanwhile,ZrMgMo3O12 shows low non-hygroscopicity and negative thermal expansion,but low softening temperature.After substituting amount of Y^3+for(ZrMg)^6+in ZrMgMo3O12(x=0.8),the softening temperature increases remarkably(750 K to 830 K)and it presents near zero thermal expansion.