The behaviors of the precipitation and decomposition of carbides in AISI M2 high-speed steel modified by nitrogen and mischmetal were investigated using DSC, XRD, SEM and TEM. The as-cast microstructure of the experim...The behaviors of the precipitation and decomposition of carbides in AISI M2 high-speed steel modified by nitrogen and mischmetal were investigated using DSC, XRD, SEM and TEM. The as-cast microstructure of the experimental steel consists of dendrites of iron matrix, networks of eutectic carbides and secondary carbides. The average distance between networks is about 34 μm. The carbides mainly include M_2C, M(C,N) and M_6C, and their relative contents are 58.5%, 30.3% and 11.2%, respectively. The average spacing between the M_2C fibers is 1.5 μm. The decomposition of M_2C occurs from 897.2 to 1221.5 ℃(heating rate of 200 ℃/h). Some precipitated carbide particles occur in the M_2C matrix after holding for 15 min at 1100 ℃. With increasing holding time, the carbide fibers neck down more and more obviously until they are broken down. The spectral peaks of M_2C almost disappear after holding for 60 min. The spectral peaks of M_6C gradually strengthen with the holding time, and the relative content of M_6C increases to 79.8% after holding for 60 min. After holding for 180 min, the carbide fibers disappear, and the decomposition products consist of fine carbide particles(about 300 nm) and short rod-like carbides(about 3.5 μm).展开更多
The delayed fracture behavior of medium carbon high strength spring steel containing different amounts of boron （0. 000 5%, 0. 001 6 %） was studied using sustained load delayed fracture test. The results show that d...The delayed fracture behavior of medium carbon high strength spring steel containing different amounts of boron （0. 000 5%, 0. 001 6 %） was studied using sustained load delayed fracture test. The results show that delayed fracture resistance of boron containing steels is higher than that of conventional steel 60Si2MnA at the same strength level and it increases with the increase of boron eontent from 0. 000 5% to 0. 001 6%. The delayed fracture mode is mainly intergranular in the boron containing steels tempered at 350℃, which indicates that the addition of boron does not change the fracture character. However, the increase of boron content enlarges the size of the crack initia tion area. Further study of phase analysis indicates that most boron is in solid solution, and only a very small quantity of boron is in the M3 （C, B） phase.展开更多
The precipitation characteristics and effect on strengthening mechanism of Cu-rich phases during short-time and long-time aging for Super 304H steels with different Cu content were investigated using X-ray diffraction...The precipitation characteristics and effect on strengthening mechanism of Cu-rich phases during short-time and long-time aging for Super 304H steels with different Cu content were investigated using X-ray diffraction （XRD）, scanning electron microscope （SEM） and transmission electron microscope （TEM）. The results show that the size of Cu-rich phase particles increases, the interspace of Cu-rich phase particles decreases and the density of Curich phases increases with the increase of Cu content during short-time aging （approximately 800 h） at 650℃ for Super 304H steels. During long-time aging （more than 2 000 h） at 650 ℃, Cu-rich phase precipitates sufficiently and the strengthening effect of Cu-rich phase is preferable in Super 304H steel containing Cu of 4%. The strengthening effect of Cu-rich phase in Super 304H steels containing Cu of 2.2% or 5% is weaker than that with Cu of 4% during long-time aging （more than 2 000 h）.展开更多
基金Project(E2016203256)supported by the Natural Science Foundation of Hebei Province,China
文摘The behaviors of the precipitation and decomposition of carbides in AISI M2 high-speed steel modified by nitrogen and mischmetal were investigated using DSC, XRD, SEM and TEM. The as-cast microstructure of the experimental steel consists of dendrites of iron matrix, networks of eutectic carbides and secondary carbides. The average distance between networks is about 34 μm. The carbides mainly include M_2C, M(C,N) and M_6C, and their relative contents are 58.5%, 30.3% and 11.2%, respectively. The average spacing between the M_2C fibers is 1.5 μm. The decomposition of M_2C occurs from 897.2 to 1221.5 ℃(heating rate of 200 ℃/h). Some precipitated carbide particles occur in the M_2C matrix after holding for 15 min at 1100 ℃. With increasing holding time, the carbide fibers neck down more and more obviously until they are broken down. The spectral peaks of M_2C almost disappear after holding for 60 min. The spectral peaks of M_6C gradually strengthen with the holding time, and the relative content of M_6C increases to 79.8% after holding for 60 min. After holding for 180 min, the carbide fibers disappear, and the decomposition products consist of fine carbide particles(about 300 nm) and short rod-like carbides(about 3.5 μm).
基金Item Sponsored by National Key Fundamental Research and Development Programme of China (2004CB619104)
文摘The delayed fracture behavior of medium carbon high strength spring steel containing different amounts of boron （0. 000 5%, 0. 001 6 %） was studied using sustained load delayed fracture test. The results show that delayed fracture resistance of boron containing steels is higher than that of conventional steel 60Si2MnA at the same strength level and it increases with the increase of boron eontent from 0. 000 5% to 0. 001 6%. The delayed fracture mode is mainly intergranular in the boron containing steels tempered at 350℃, which indicates that the addition of boron does not change the fracture character. However, the increase of boron content enlarges the size of the crack initia tion area. Further study of phase analysis indicates that most boron is in solid solution, and only a very small quantity of boron is in the M3 （C, B） phase.
基金Sponsored by National Science and Technology Support Plan of China (2007BAE51B02)
文摘The precipitation characteristics and effect on strengthening mechanism of Cu-rich phases during short-time and long-time aging for Super 304H steels with different Cu content were investigated using X-ray diffraction （XRD）, scanning electron microscope （SEM） and transmission electron microscope （TEM）. The results show that the size of Cu-rich phase particles increases, the interspace of Cu-rich phase particles decreases and the density of Curich phases increases with the increase of Cu content during short-time aging （approximately 800 h） at 650℃ for Super 304H steels. During long-time aging （more than 2 000 h） at 650 ℃, Cu-rich phase precipitates sufficiently and the strengthening effect of Cu-rich phase is preferable in Super 304H steel containing Cu of 4%. The strengthening effect of Cu-rich phase in Super 304H steels containing Cu of 2.2% or 5% is weaker than that with Cu of 4% during long-time aging （more than 2 000 h）.