Perovskite oxide La_(0.6)Ca_(0.4)Fe_(0.8)Ni_(0.2)O_(3-δ)(LCFN)has been used in symmetric solid oxide cells(SSOCs)to obtain good electrochemical performance in both fuel cells(SOFCs)and electrolysis cells(SOECs)modes....Perovskite oxide La_(0.6)Ca_(0.4)Fe_(0.8)Ni_(0.2)O_(3-δ)(LCFN)has been used in symmetric solid oxide cells(SSOCs)to obtain good electrochemical performance in both fuel cells(SOFCs)and electrolysis cells(SOECs)modes.However,its structural stability still faces challenges and the electrocatalytic activity also needs to be further improved.Herein,tungsten-doped La_(0.6)Ca_(0.4)Fe_(0.7)Ni_(0.2)W_(0.1)0_(3-δ)(LCFNW)perovskite oxide material was synthesized which exhibits good structural stability under H_(2)and superior electrochemical performance as an electrode for SSOCs.In SOFCs mode,the cell achieved the maximum power density of 0.58 W·cm^(-2)with wet H_(2)as fuel at 850℃.In SOECs mode,the current density can reach 1.81 A·cm^(-2)for pure CO_(2)electrolysis at 2 V.Moreover,the SSOCs exhibits outstanding long-term stability in both SOFCs and SOECs modes,proving that doping W in perovskite oxide is an effective strategy to enhance the catalytic activity and stability of the electrode.The LCFNW material developed in this work shows promising prospect as an electrode candidate for SSOCs.展开更多
基金financial support from National Key R&D Program for Young Scientists(2021YFA1501900)National Natural Science Foundation of China(52272257)+4 种基金Material Science and Engineering Discipline Guidance Fund of China University of Mining and Technology(CUMTMS202203)Foundation of State Key Laboratory of Clean and Efficient Coal Utilization,Taiyuan University of Technology(Grant No.SKL2022008)the Jiangsu Provincial Shuangchuang Doctor Program(JSSCBS20211224)Young Elite Scientists Sponsorship Program by(CAST2022QNRC001)the Open Sharing Fund for the Large-scale Instruments(DYGX-2021026)and Equipments of China University of Mining and Technology(CUMT)Analytical for sample characterizations assistance。
文摘Perovskite oxide La_(0.6)Ca_(0.4)Fe_(0.8)Ni_(0.2)O_(3-δ)(LCFN)has been used in symmetric solid oxide cells(SSOCs)to obtain good electrochemical performance in both fuel cells(SOFCs)and electrolysis cells(SOECs)modes.However,its structural stability still faces challenges and the electrocatalytic activity also needs to be further improved.Herein,tungsten-doped La_(0.6)Ca_(0.4)Fe_(0.7)Ni_(0.2)W_(0.1)0_(3-δ)(LCFNW)perovskite oxide material was synthesized which exhibits good structural stability under H_(2)and superior electrochemical performance as an electrode for SSOCs.In SOFCs mode,the cell achieved the maximum power density of 0.58 W·cm^(-2)with wet H_(2)as fuel at 850℃.In SOECs mode,the current density can reach 1.81 A·cm^(-2)for pure CO_(2)electrolysis at 2 V.Moreover,the SSOCs exhibits outstanding long-term stability in both SOFCs and SOECs modes,proving that doping W in perovskite oxide is an effective strategy to enhance the catalytic activity and stability of the electrode.The LCFNW material developed in this work shows promising prospect as an electrode candidate for SSOCs.