High-entropy diborides(HEBs)are considered as promising high-temperature structure materials owing to their high melting point and excellent thermal stability.However,the intrinsic brittleness is the main obstacle tha...High-entropy diborides(HEBs)are considered as promising high-temperature structure materials owing to their high melting point and excellent thermal stability.However,the intrinsic brittleness is the main obstacle that seriously limits their practical applications.To overcome with this obstacle,carbon fibers(Cf)with outstanding mechanical properties are used in the present work as a first attempt to improve the damage tolerance of HEBs.The as-prepared C_(f)/(Ti_(0.2)Zr_(0.2)Hf_(0.2)Nb_(0.2)Ta_(0.2))B_(2)–SiC composite(C_(f)/HEB–SiC)shows high relative density(97.9%)and good mechanical properties with flexural strength of 411±3 MPa and fracture toughness of 6.15±0.11 MPa·m^(1/2).More importantly,the damage tolerance parameter(Dt)has increased from 0.10 m^(1/2) for HEB–SiC to 0.29 m^(1/2) for C_(f)/HEB–SiC.Through microstructural analysis and Vickers indentation of the composite,the toughening mechanisms are disclosed.The carbon fibers coated with carbon coatings demonstrate unique capacity for prolonging the crack propagation path,which promotes the reliability of the composite effectively.Moreover,the C_(f)/(Ti_(0.2)Zr_(0.2)Hf_(0.2)Nb_(0.2)Ta_(0.2))B_(2)–SiC composite also exhibits good static oxidation resistance in the temperature range of 1100–1500℃in air due to the formation of the protective oxide layer constituting of multicomponent oxides(Zr)HfTiO4 and(Zr)Hf_(6)Ta_(2)O_(17) embedded in a continuous SiO_(2) glass.These results are promising,and this primary work can be used as a reference to the synthesis of C_(f)/HEBs for thermal protection materials under hightemperature serving conditions.展开更多
基金supported by the National Natural Science Foundation of China(Grant Nos.52172075 and 52302074)the Outstanding Youth Foundation of Henan Province(Grant No.202300410355)+4 种基金the Program for Innovative Research Team in Science and Technology in Universities of Henan Province(Grant No.23IRTSTHN001)the China Postdoctoral Science Foundation(Grant No.2021M702931)the Science Foundation of National Key Laboratory of Science and Technology on Advanced Composites in Special Environments(Grant No.JCKYS2022603C024)the Natural Science Foundation of Henan Province(Grant No.232300421323)the Henan Provincial Science and Technology Research and Development Plan Joint Fund(Grant No.222301420031).
文摘High-entropy diborides(HEBs)are considered as promising high-temperature structure materials owing to their high melting point and excellent thermal stability.However,the intrinsic brittleness is the main obstacle that seriously limits their practical applications.To overcome with this obstacle,carbon fibers(Cf)with outstanding mechanical properties are used in the present work as a first attempt to improve the damage tolerance of HEBs.The as-prepared C_(f)/(Ti_(0.2)Zr_(0.2)Hf_(0.2)Nb_(0.2)Ta_(0.2))B_(2)–SiC composite(C_(f)/HEB–SiC)shows high relative density(97.9%)and good mechanical properties with flexural strength of 411±3 MPa and fracture toughness of 6.15±0.11 MPa·m^(1/2).More importantly,the damage tolerance parameter(Dt)has increased from 0.10 m^(1/2) for HEB–SiC to 0.29 m^(1/2) for C_(f)/HEB–SiC.Through microstructural analysis and Vickers indentation of the composite,the toughening mechanisms are disclosed.The carbon fibers coated with carbon coatings demonstrate unique capacity for prolonging the crack propagation path,which promotes the reliability of the composite effectively.Moreover,the C_(f)/(Ti_(0.2)Zr_(0.2)Hf_(0.2)Nb_(0.2)Ta_(0.2))B_(2)–SiC composite also exhibits good static oxidation resistance in the temperature range of 1100–1500℃in air due to the formation of the protective oxide layer constituting of multicomponent oxides(Zr)HfTiO4 and(Zr)Hf_(6)Ta_(2)O_(17) embedded in a continuous SiO_(2) glass.These results are promising,and this primary work can be used as a reference to the synthesis of C_(f)/HEBs for thermal protection materials under hightemperature serving conditions.
