A 10 × 10 solar-blind ultraviolet(UV) imaging array with double-layer wire structure was prepared based on Ga_(2)O_(3) film grown by atomic layer deposition. These single detection units in the array exhibit exce...A 10 × 10 solar-blind ultraviolet(UV) imaging array with double-layer wire structure was prepared based on Ga_(2)O_(3) film grown by atomic layer deposition. These single detection units in the array exhibit excellent performance at 3 V: photo-todark current ratio(PDCR) of 5.5 × 10^(5), responsivity(R) of 4.28 A/W, external quantum efficiency(EQE) of 2.1 × 10^(3)%, detectivity(D*) of 1.5 × 10^(14) Jones, and fast response time. The photodetector array shows high uniformity under different light intensity and low operating bias. The array also has good temperature stability. Under 300 ℃, it still presents clear imaging and keeps high R of 34.4 and 6.45 A/W at 5 and 1 V, respectively. This work provides a new insight for the large-scale array of Ga_(2)O_(3) solarblind UV detectors.展开更多
基金supported by Natural Science Basic Research Program of Shaanxi Province of China (No. 2023-JCYB-574)National Natural Science Foundation of China (Grant No. 62304178)。
文摘A 10 × 10 solar-blind ultraviolet(UV) imaging array with double-layer wire structure was prepared based on Ga_(2)O_(3) film grown by atomic layer deposition. These single detection units in the array exhibit excellent performance at 3 V: photo-todark current ratio(PDCR) of 5.5 × 10^(5), responsivity(R) of 4.28 A/W, external quantum efficiency(EQE) of 2.1 × 10^(3)%, detectivity(D*) of 1.5 × 10^(14) Jones, and fast response time. The photodetector array shows high uniformity under different light intensity and low operating bias. The array also has good temperature stability. Under 300 ℃, it still presents clear imaging and keeps high R of 34.4 and 6.45 A/W at 5 and 1 V, respectively. This work provides a new insight for the large-scale array of Ga_(2)O_(3) solarblind UV detectors.