Nano-nitramine explosives(RDX.HMX.CL-20) are produced on a bi-directional grinding mill.The scanning electron microscope(SEM)observations show that the prepared particles are semi-spherical,and the narrow size distrib...Nano-nitramine explosives(RDX.HMX.CL-20) are produced on a bi-directional grinding mill.The scanning electron microscope(SEM)observations show that the prepared particles are semi-spherical,and the narrow size distributions are characterized using the laser particle size analyzer.Compared with the micron-sized samples,the nano-products show obvious decrease in friction and impact sensitivities.In the case of shock sensitivities,nano-products have lower values by 59.9%(RDX),56.4%(HMX),and 58.1%(CL-20),respectively.When nano-RDX and nano-HMX are used in plastic bonded explosives(PBX) as alternative materials of micron-sized particles,their shock sensitivities are significantly decreased by 24.5%(RDX) and 22.9%(HMX),and their detonation velocities are increased by about 1.7%.Therefore,it is expected to promote the application of nano-nitramine explosives in PBXs and composite modified double-based propellants(CMDBs) so that some of their properties would be improved.展开更多
Nano hexahydro-1,3,5-trinitro-1,3,5-triazine(RDX) was prepared using a bi-directional rotation mill and dried under different conditions(liquid, temperature and drying). It shows that the samples cake seriously and th...Nano hexahydro-1,3,5-trinitro-1,3,5-triazine(RDX) was prepared using a bi-directional rotation mill and dried under different conditions(liquid, temperature and drying). It shows that the samples cake seriously and the particles grow up obviously by ordinary drying in different liquids at 70 C, which occurs again after vacuum drying. With the increase of temperature, the degrees of caking and aggregation are enhanced.Well dispersed sample maintaining constant particle size is extracted by supercritical drying, especially freeze drying. Furthermore, the mechanical sensitivities of I-RDX, O-RDX and F-RDX, of which the average sizes are 88.03 mm, 15.32 mm and 0.16 mm, respectively, are evaluated. Compared with I-RDX, the friction, impact and shock sensitivities of O-RDX are slightly lower. However, the friction, impact and shock sensitivities of F-RDX are reduced by 30%, 99.0% and 59.9%, respectively.展开更多
文摘Nano-nitramine explosives(RDX.HMX.CL-20) are produced on a bi-directional grinding mill.The scanning electron microscope(SEM)observations show that the prepared particles are semi-spherical,and the narrow size distributions are characterized using the laser particle size analyzer.Compared with the micron-sized samples,the nano-products show obvious decrease in friction and impact sensitivities.In the case of shock sensitivities,nano-products have lower values by 59.9%(RDX),56.4%(HMX),and 58.1%(CL-20),respectively.When nano-RDX and nano-HMX are used in plastic bonded explosives(PBX) as alternative materials of micron-sized particles,their shock sensitivities are significantly decreased by 24.5%(RDX) and 22.9%(HMX),and their detonation velocities are increased by about 1.7%.Therefore,it is expected to promote the application of nano-nitramine explosives in PBXs and composite modified double-based propellants(CMDBs) so that some of their properties would be improved.
文摘Nano hexahydro-1,3,5-trinitro-1,3,5-triazine(RDX) was prepared using a bi-directional rotation mill and dried under different conditions(liquid, temperature and drying). It shows that the samples cake seriously and the particles grow up obviously by ordinary drying in different liquids at 70 C, which occurs again after vacuum drying. With the increase of temperature, the degrees of caking and aggregation are enhanced.Well dispersed sample maintaining constant particle size is extracted by supercritical drying, especially freeze drying. Furthermore, the mechanical sensitivities of I-RDX, O-RDX and F-RDX, of which the average sizes are 88.03 mm, 15.32 mm and 0.16 mm, respectively, are evaluated. Compared with I-RDX, the friction, impact and shock sensitivities of O-RDX are slightly lower. However, the friction, impact and shock sensitivities of F-RDX are reduced by 30%, 99.0% and 59.9%, respectively.