NASICON-type Na_(3)V_(2)(PO_(4))_(3) is a promising electrode material for developing advanced sodium-ion batteries.Preparing Na_(3)V_(2)(PO_(4))_(3) with good performance by a cost-effective and large-scale method is...NASICON-type Na_(3)V_(2)(PO_(4))_(3) is a promising electrode material for developing advanced sodium-ion batteries.Preparing Na_(3)V_(2)(PO_(4))_(3) with good performance by a cost-effective and large-scale method is significant for industrial applications.In this work,a porous Na_(3)V_(2)(PO_(4))_(3)/C cathode material with excellent electrochemical performance is successfully prepared by an agar-gel combined with freeze-drying method.The Na_(3)V_(2)(PO_(4))_(3)/C cathode displayed specific capacities of 113.4 mAh·g^(-1),107.0 mAh·g^(-1) and 87.1 mAh·g^(-1) at 0.1 C,1 C and 10 C,respectively.For the first time,the 500-mAh soft-packed symmetrical sodium-ion batteries based on Na_(3)V_(2)(PO_(4))_(3)/C electrodes are successfully fabricated.The 500-mAh symmetrical batteries exhibit outstanding low temperature performance with a capacity retention of 83%at 0℃ owing to the rapid sodium ion migration ability and structural stability of Na_(3)V_(2)(PO_(4))_(3)/C.Moreover,the thermal runaway features are revealed by accelerating rate calorimetry(ARC)test for the first time.Thermal stability and safety of the symmetrical batteries are demonstrated to be better than lithium-ion batteries and some reported sodium-ion batteries.Our work makes it clear that the soft-packed symmetrical sodium ion batteries based on Na_(3)V_(2)(PO_(4))_(3)/C have a prospect of practical application in high safety requirement fields.展开更多
基金This work was supported by the National Key Research and Development Program(2016YFB0901505)the Natural Science Foundation of China(22005190,21938005)+1 种基金the Science&Technology Commission of Shanghai Municipality(19DZ1205500)Zhejiang Key Research and Development Program(2020C01128).
文摘NASICON-type Na_(3)V_(2)(PO_(4))_(3) is a promising electrode material for developing advanced sodium-ion batteries.Preparing Na_(3)V_(2)(PO_(4))_(3) with good performance by a cost-effective and large-scale method is significant for industrial applications.In this work,a porous Na_(3)V_(2)(PO_(4))_(3)/C cathode material with excellent electrochemical performance is successfully prepared by an agar-gel combined with freeze-drying method.The Na_(3)V_(2)(PO_(4))_(3)/C cathode displayed specific capacities of 113.4 mAh·g^(-1),107.0 mAh·g^(-1) and 87.1 mAh·g^(-1) at 0.1 C,1 C and 10 C,respectively.For the first time,the 500-mAh soft-packed symmetrical sodium-ion batteries based on Na_(3)V_(2)(PO_(4))_(3)/C electrodes are successfully fabricated.The 500-mAh symmetrical batteries exhibit outstanding low temperature performance with a capacity retention of 83%at 0℃ owing to the rapid sodium ion migration ability and structural stability of Na_(3)V_(2)(PO_(4))_(3)/C.Moreover,the thermal runaway features are revealed by accelerating rate calorimetry(ARC)test for the first time.Thermal stability and safety of the symmetrical batteries are demonstrated to be better than lithium-ion batteries and some reported sodium-ion batteries.Our work makes it clear that the soft-packed symmetrical sodium ion batteries based on Na_(3)V_(2)(PO_(4))_(3)/C have a prospect of practical application in high safety requirement fields.