Magnetic properties and magnetic entropy change of perovskite manganites La_(0.9-x)Eu_xSr_(0.1)MnO_3(x=0.000,0.075) by experimental method and numerical fitting

Polycrystalline samples La_(0.9-x)EuxSr_(0.1)MnO_3(x = 0.000, 0.075) were prepared by the standard solid-state reaction method. The results show that the samples preform a characteristic of clusters spin-glass state at low temperature. The samples show a characteristic of ferromagnetism(FM) characteristic in the temperature range of 15-125 K and 15-150 K respectively; the samples show preformed clusters in the temperature range of 125-343 K and 150-325 K, respectively, the samples show paramagnetism(PM)characteristic above 343 and 325 K, respectively. The second-order transitions are found at 118 and 135 K for undoped and doped sample, respectively. When the applied magnetic field is 7 T, the maximum magnetic entropy change |△S_M| value of the samples is near the Curie temperature(Tc), and the value of|△S_M| reaches 2.76 and 3.03 J/(K kg), respectively. In addition, the relative cooling power(RCP) is found to be 425.28 and 443.53 J/kg. The numerical fitting data fit well with experimental data. These results indicate that both the samples have the potential to realize magnetic refrigeration in the high temperature region(T > 77 K).

Structure,magnetism and magnetic thermal properties of heavy rare earth Tb1-xTmxFeO3(x=0.00,0.15,0.25) polycrystalline samples

Tb1-xTmxFeO3(x = 0.00,0.15,0.25) polycrystalline series were synthesized using a solid-state reaction.Our results show that all three prepared samples are in a distorted orthogonal structure and their space group is pbnm.When the Tm3+doping amount increases,the characteristics of the spin-flip of the sample decreases following an initial increase at the beginning;the antiferromagnetic property almost reaches zero;the magnetization decreases at the beginning but increases later on.The maximum magnetic entropy change and magnetic refrigeration effect RCP are reduced at varying degrees.Under a 7 T magnetic field,the maximum magnetic entropy change,△Smax,for the three samples of Tb1-xTmxFeO3 with x=0.00,0.15,0.25 is 13.78,-9.28,and 10.69 J/(K·kg),respectively;the magnetic refrigeration capacity(RCP) is 316.85,175.2,and 297.60 J/kg,respectively.In summary,doping with the element Tm reduces △Smax and RCP of the sample.Since the maximum magnetic entropy change and the cooling capacity for the three samples are relatively large,they can be used as an alternative for magnetic refrigerants.