Doped elements in alloys significantly impact their performance.Conventional methods usually sputter the surface material of the sample,or their performance is limited to the surface of alloys owing to their poor pene...Doped elements in alloys significantly impact their performance.Conventional methods usually sputter the surface material of the sample,or their performance is limited to the surface of alloys owing to their poor penetration ability.The X-ray K-edge subtraction(KES)method exhibits great potential for the nondestructive in situ detection of element contents in alloys.However,the signal of doped elements usually deteriorates because of the strong absorption of the principal component and scattering of crystal grains.This in turn prevents the extensive application of X-ray KES imaging to alloys.In this study,methods were developed to calibrate the linearity between the grayscale of the KES image and element content.The methods were aimed at the sensitive analysis of elements in alloys.Furthermore,experiments with phantoms and alloys demonstrated that,after elaborate calibration,X-ray KES imaging is capable of nondestructive and sensitive analysis of doped elements in alloys.展开更多
TiC-316 L metal matrix composites were successfully printed with an epoxy resin-absolute ethanol system by direct ink writing(DIW) process in this study.Microstructure and fracture morphology of the samples were obser...TiC-316 L metal matrix composites were successfully printed with an epoxy resin-absolute ethanol system by direct ink writing(DIW) process in this study.Microstructure and fracture morphology of the samples were observed by a scanning electron microscope(SEM).Also,the relative density,hardness and transverse rupture strength(TRS) of the sintered samples were tested.The results show that the samples prepared with a new epoxy resin-absolute ethanol system by the DIW process have high solid content of printing slurry,good surface roughness,high relative density and high strength.The solid content of the slurry suitable for DIW was 60 vol%,and the internal diameter of the nozzle was set to 0.4 mm,the printing speed was set to 30 mm·s^(-1),and the layer height was set to 0.36 mm.For the sample with 35 wt% TiC-316 L,the relative density,hardness and TRS of the sintered sample can reach 99.3%,HRA 79.5 and 1438 MPa,respectively.展开更多
基金supported by the National Key Research and Development Program of China(Nos.2017YFA0403801,2017YFA0206004,2018YFC1200204)the National Natural Science Foundation of China(NSFC)(Nos.81430087,11775297,U1932205).
文摘Doped elements in alloys significantly impact their performance.Conventional methods usually sputter the surface material of the sample,or their performance is limited to the surface of alloys owing to their poor penetration ability.The X-ray K-edge subtraction(KES)method exhibits great potential for the nondestructive in situ detection of element contents in alloys.However,the signal of doped elements usually deteriorates because of the strong absorption of the principal component and scattering of crystal grains.This in turn prevents the extensive application of X-ray KES imaging to alloys.In this study,methods were developed to calibrate the linearity between the grayscale of the KES image and element content.The methods were aimed at the sensitive analysis of elements in alloys.Furthermore,experiments with phantoms and alloys demonstrated that,after elaborate calibration,X-ray KES imaging is capable of nondestructive and sensitive analysis of doped elements in alloys.
基金financially supported by Heyuan Science and Technology Project(No.HEKE 000781)the Science and Technology Projects of Guangdong Province(No.2016B090914001)Jihua Laboratory Project“Additive Manufacturing for Difficulty-to-Machine Materials”(No.X190061UZ190)。
文摘TiC-316 L metal matrix composites were successfully printed with an epoxy resin-absolute ethanol system by direct ink writing(DIW) process in this study.Microstructure and fracture morphology of the samples were observed by a scanning electron microscope(SEM).Also,the relative density,hardness and transverse rupture strength(TRS) of the sintered samples were tested.The results show that the samples prepared with a new epoxy resin-absolute ethanol system by the DIW process have high solid content of printing slurry,good surface roughness,high relative density and high strength.The solid content of the slurry suitable for DIW was 60 vol%,and the internal diameter of the nozzle was set to 0.4 mm,the printing speed was set to 30 mm·s^(-1),and the layer height was set to 0.36 mm.For the sample with 35 wt% TiC-316 L,the relative density,hardness and TRS of the sintered sample can reach 99.3%,HRA 79.5 and 1438 MPa,respectively.