The mineralogical phase transformation of a low-grade nickel laterite ore during pre-roasting process and the extraction of silicon during alkaline leaching process were investigated.The results indicate that the reac...The mineralogical phase transformation of a low-grade nickel laterite ore during pre-roasting process and the extraction of silicon during alkaline leaching process were investigated.The results indicate that the reaction activity of nickel ores is effectively improved by pre-roasting at650°C for2h,because of the transformation of lizardite into magnesium olivine and protoenstatite.When finely ground ore samples(44-61μm)pre-roasted firstly react with sodium hydroxide solution(60g/L)with a solid/liquid ratio of1:5at140°C for120min,the extraction of silicon can reach89.89%,and the other valuable elements of magnesium,iron and nickel are accumulated in the solid residues.The leaching kinetics of nickel laterite ore can be described successfully by the diffusion through the product layer control model.The activation energy is calculated to be11.63kJ/mol and the kinetics equation can be expressed as1-3(1-x)2/3+2(1-x)=13.53×10-2exp[-11.63/(RT)]t.展开更多
Nickel-based superalloy was treated with molten zinc for the selective extraction of nickel.The effects of heating temperature,heating time,and the mass ratio of zinc to superalloy on the extraction of metals in the s...Nickel-based superalloy was treated with molten zinc for the selective extraction of nickel.The effects of heating temperature,heating time,and the mass ratio of zinc to superalloy on the extraction of metals in the superalloy were investigated.An extraction rate of 95.2%for nickel,55.4%for iron and 30.4%for chromium,but low extraction rates of the refractory metals(titanium(Ti),molybdenum(Mo),and niobium(Nb))were obtained under the optimal conditions of the heating temperature of 850℃,the heating time of 4 h,and the zinc/superalloy mass ratio of 10:1.In the subsequent vacuum distillation process,the obtained nickel alloy contained nickel with a purity of 73.5 wt.%after zinc removal.Moreover,the recovered zinc after the distillation process had a purity of 99.9 wt.%.The results of the investigated process indicated the possibility of extracting nickel directly from nickel-based superalloy scraps.展开更多
基金Project(2014CB643405) supported by the National Basic Research Program of ChinaProjects(51204036,51234009) supported by the National Natural Science Foundation of ChinaProject(BJ201604) supported by the Program for Top Young Talents of Higher Education Institutions of Hebei Province,China
文摘The mineralogical phase transformation of a low-grade nickel laterite ore during pre-roasting process and the extraction of silicon during alkaline leaching process were investigated.The results indicate that the reaction activity of nickel ores is effectively improved by pre-roasting at650°C for2h,because of the transformation of lizardite into magnesium olivine and protoenstatite.When finely ground ore samples(44-61μm)pre-roasted firstly react with sodium hydroxide solution(60g/L)with a solid/liquid ratio of1:5at140°C for120min,the extraction of silicon can reach89.89%,and the other valuable elements of magnesium,iron and nickel are accumulated in the solid residues.The leaching kinetics of nickel laterite ore can be described successfully by the diffusion through the product layer control model.The activation energy is calculated to be11.63kJ/mol and the kinetics equation can be expressed as1-3(1-x)2/3+2(1-x)=13.53×10-2exp[-11.63/(RT)]t.
基金financial supports from the National Natural Science Foundation of China(Nos.51922108,51874371,51904350)the Hunan Natural Science Foundation,China(No.2019JJ20031)the Hunan Key Research and Development Program,China(No.2019SK2061)。
文摘Nickel-based superalloy was treated with molten zinc for the selective extraction of nickel.The effects of heating temperature,heating time,and the mass ratio of zinc to superalloy on the extraction of metals in the superalloy were investigated.An extraction rate of 95.2%for nickel,55.4%for iron and 30.4%for chromium,but low extraction rates of the refractory metals(titanium(Ti),molybdenum(Mo),and niobium(Nb))were obtained under the optimal conditions of the heating temperature of 850℃,the heating time of 4 h,and the zinc/superalloy mass ratio of 10:1.In the subsequent vacuum distillation process,the obtained nickel alloy contained nickel with a purity of 73.5 wt.%after zinc removal.Moreover,the recovered zinc after the distillation process had a purity of 99.9 wt.%.The results of the investigated process indicated the possibility of extracting nickel directly from nickel-based superalloy scraps.