To improve the damping capacities of metals and alloys, the microstructures and damping capacities of ZA27 alloy modified by Zr were studied, and the damping capacities at room tempemture were measured by using cantil...To improve the damping capacities of metals and alloys, the microstructures and damping capacities of ZA27 alloy modified by Zr were studied, and the damping capacities at room tempemture were measured by using cantilever beam techniques. The experiment results show that Zr can refine the Al-rich primary phase and improve the damping Capacities saliently. Compared with the un-modified one, the damping capacity of ZA27 alloy modified by 0.3wt%Zr received 90 percent increment. The high damping capacities are attributed primarily to grain ablement and the increasing of phase interfaces.展开更多
A high strain rate multi-directional impact forging(MDIF) was applied to a solutionized Mg-Gd-Y-Zr alloy in the temperature range of 350-500℃.Results demonstrate that the dominant deformation mode is twinning at a te...A high strain rate multi-directional impact forging(MDIF) was applied to a solutionized Mg-Gd-Y-Zr alloy in the temperature range of 350-500℃.Results demonstrate that the dominant deformation mode is twinning at a temperature below 400℃,whereas at a medium temperature of 450℃ considerable continuous dynamic recrystallization was promoted by{10-12} extension twins.At a higher temperature of 500℃,twinning activation was suppressed.New DRX grains were observed but their sizes were much bigger than those resulting from the MDIFed 50 passes at 450℃,which are ascribed to the larger grain boundary mobility and atomic diffusion at 500℃.Moreover,a non-basal weak texture was gained afterward MDIF at each temperature,which is credited to the MDIF process and the minor strain applied in each pass.展开更多
文摘To improve the damping capacities of metals and alloys, the microstructures and damping capacities of ZA27 alloy modified by Zr were studied, and the damping capacities at room tempemture were measured by using cantilever beam techniques. The experiment results show that Zr can refine the Al-rich primary phase and improve the damping Capacities saliently. Compared with the un-modified one, the damping capacity of ZA27 alloy modified by 0.3wt%Zr received 90 percent increment. The high damping capacities are attributed primarily to grain ablement and the increasing of phase interfaces.
基金supported by the National Key Research and Development Program of China(No.2016YFB0301104)the National Natural Science Foundation of China(NSFC,Nos.51301173,51531002 and 51601193)the National Basic Research Program of China(973 Program,No.2013CB632202).
文摘A high strain rate multi-directional impact forging(MDIF) was applied to a solutionized Mg-Gd-Y-Zr alloy in the temperature range of 350-500℃.Results demonstrate that the dominant deformation mode is twinning at a temperature below 400℃,whereas at a medium temperature of 450℃ considerable continuous dynamic recrystallization was promoted by{10-12} extension twins.At a higher temperature of 500℃,twinning activation was suppressed.New DRX grains were observed but their sizes were much bigger than those resulting from the MDIFed 50 passes at 450℃,which are ascribed to the larger grain boundary mobility and atomic diffusion at 500℃.Moreover,a non-basal weak texture was gained afterward MDIF at each temperature,which is credited to the MDIF process and the minor strain applied in each pass.