The morphologies and hydration properties of MgO expansive material at different curing temperatures were investigated.When the curing temperature varies from 25℃to 50℃,the conductivity of MgO rises from 40 to 80μs...The morphologies and hydration properties of MgO expansive material at different curing temperatures were investigated.When the curing temperature varies from 25℃to 50℃,the conductivity of MgO rises from 40 to 80μs/cm,the hydration product of MgO expansive material curing in water for 28 days is from 1.5—2 mm to 2—2.5μm in length through SEM observation,and the expansion of pastes with 5%of the magnesium oxide is from 0.36%up to 1.01%,it is increased by 2.78 times.When the content of cement paste increases to 95%and cured in water for 90 days,the brucite forms as hexaflaggy?shaped crystal,which is less than 0.1μm and tends to aggregates.The effect of curing temperature on the hydration of MgO expansive material is obvious.展开更多
The mechanisms and processes of sulfate attack on roller compacted concrete(RCC)with MgO expansive agent are proposed by investigating the microstructure and hydration products in specimens immersed in 5%sodium sulfat...The mechanisms and processes of sulfate attack on roller compacted concrete(RCC)with MgO expansive agent are proposed by investigating the microstructure and hydration products in specimens immersed in 5%sodium sulfate solution for one year with the optical micrograph,scanning electron microscopy(SEM)and scanning electron microscopy-energy dispersive spectrometer(SEM-EDS).The results show that the deterioration of concrete due to the sulfate attack is mainly loss of stiffness,strength and adhesion,and expansion cracking is mainly caused by the formation of gypsum and ettringite.In the presence of MgO expansive agent,the microstructures of RCC can be improved by hydration and un-hydrated products,the large pores and permeability are reduced,and the resistance to sulfate corrosion of concrete and durability of hydraulic structure are improved slightly.展开更多
基金the Research Center on Levee Safety Disaster Prevention, MWR (No. 2019004)High-level Talent Project Funding Scheme of Jiangsu (No. XCL-CXTD-007)+3 种基金China Postdoctoral Science Foundation (No. 2018M630559)the National Natural Science Foundation of China (No. 51908285)the Fundamental Research Nantong Metro Group Co., Ltdthe traffic construction science and technology project of Shanxi (No. 16-2-08) for its financial support in this project
文摘The morphologies and hydration properties of MgO expansive material at different curing temperatures were investigated.When the curing temperature varies from 25℃to 50℃,the conductivity of MgO rises from 40 to 80μs/cm,the hydration product of MgO expansive material curing in water for 28 days is from 1.5—2 mm to 2—2.5μm in length through SEM observation,and the expansion of pastes with 5%of the magnesium oxide is from 0.36%up to 1.01%,it is increased by 2.78 times.When the content of cement paste increases to 95%and cured in water for 90 days,the brucite forms as hexaflaggy?shaped crystal,which is less than 0.1μm and tends to aggregates.The effect of curing temperature on the hydration of MgO expansive material is obvious.
基金supported by the High-Level Talent Project Funding Scheme,Post-doctoral fund of China and Jiangsu (Nos.1301057B,2014M551588)the Fundamental Research Funds Universities(No.NS2015010)
文摘The mechanisms and processes of sulfate attack on roller compacted concrete(RCC)with MgO expansive agent are proposed by investigating the microstructure and hydration products in specimens immersed in 5%sodium sulfate solution for one year with the optical micrograph,scanning electron microscopy(SEM)and scanning electron microscopy-energy dispersive spectrometer(SEM-EDS).The results show that the deterioration of concrete due to the sulfate attack is mainly loss of stiffness,strength and adhesion,and expansion cracking is mainly caused by the formation of gypsum and ettringite.In the presence of MgO expansive agent,the microstructures of RCC can be improved by hydration and un-hydrated products,the large pores and permeability are reduced,and the resistance to sulfate corrosion of concrete and durability of hydraulic structure are improved slightly.