TEM observation of carbide precipitates in bainite has been carried out for steel 40CMD8. Specimens transformed at 350 ℃ and 450 ℃ without external stress contain respectively the lower and the upper bainite. No fun...TEM observation of carbide precipitates in bainite has been carried out for steel 40CMD8. Specimens transformed at 350 ℃ and 450 ℃ without external stress contain respectively the lower and the upper bainite. No fundamental change in carbide precipitation is observed in specimen transformed at 350 ℃ under stress of 128 MPa. The very fine cementite is found precipitated within the upper bainite plates in specimen transformed at 450 ℃ under stress of 144 MPa, which can be explained as the result of the difficulty of carbon diffusing out of the massive ferrite plate within a much shortened transformation time due to the external stress. For all the specimens examined, Bagaryatskii orientation relationship is found existing between the carbides and ferrite matrix.展开更多
文摘TEM observation of carbide precipitates in bainite has been carried out for steel 40CMD8. Specimens transformed at 350 ℃ and 450 ℃ without external stress contain respectively the lower and the upper bainite. No fundamental change in carbide precipitation is observed in specimen transformed at 350 ℃ under stress of 128 MPa. The very fine cementite is found precipitated within the upper bainite plates in specimen transformed at 450 ℃ under stress of 144 MPa, which can be explained as the result of the difficulty of carbon diffusing out of the massive ferrite plate within a much shortened transformation time due to the external stress. For all the specimens examined, Bagaryatskii orientation relationship is found existing between the carbides and ferrite matrix.