Influence of Simulated Outside-Reactor Irradiation on Anticorrosion Property of Austenitic Stainless Steel

The influence of γ-ray irradiation on the properties of inside-reactor stainless steel structures was studied by simulating the working condition of pressurized water reactor （PWR） first circuit and the outside-reactor y-ray irradiation. The result shows that the simulated outside-reactor irradiation （irradiation dose 4. 4 ）〈 104 Gy） has no influence on anticorrosion properties of solutionized SUS304 austenitic stainless steel, including intergranular corrosion （IC） and stress corrosion cracking （SCC）. Anticorrosion properties （IC, SCC） of sensitized SUS304 austenitic stainless steel are reduced by simulated outside-reactor irradiation. The longer the sensitized time is, the more obvious the influence is.

石墨烯电热薄膜材料的制备及表征

采用超临界二氧化碳剥离的方法制备了2种不同的剥离石墨烯EG-6、EG-6u,并制备了以石墨D、剥离石墨烯EG-6、EG-6u为导电填料的导电薄膜。采用扫描电镜(SEM)、拉曼光谱对原材料石墨以及导电薄膜进行表征,并对所制备薄膜进行电热特性测试。结果表明,经过超临界二氧化碳剥离之后,石墨烯片层从石墨块上剥离下来,尺寸为3~10μm。导电薄膜中石墨烯以片层方式存在,而石墨以粒状存在,片层方式的存在方式使得石墨烯片层定向排列,导电网络更丰富高效。在12 V电压下升温达到相同的空间温度,相比于导电薄膜D,导电薄膜EG-6所需功率减少22.5%,膜层温度降低9.623℃,膜层的传热效率更高,综合传热系数增大,为2.60×10-3W·cm-2·℃-1。相比于导电薄膜D,石墨烯导电薄膜的升温速率更高,升温时间更短。导电薄膜EG-6u的初始升温速率为导电薄膜D的19.3倍,升温时间为导电薄膜D的24.7%。

石墨烯及其复合材料在空气净化领域的应用研究进展

目前室内与室外的空气污染问题越来越严重,寻找有效的净化材料与技术迫在眉睫。石墨烯及其衍生物由于其特殊的结构、稳定的物理化学性能及优异的电子迁移率等,在空气净化领域发展潜能巨大。综述了石墨烯及其复合材料在空气净化领域的研究进展,并以固态、气态及微生物污染物为净化目标,主要针对材料的吸附、过滤、抗菌抑菌和光催化作用,及对石墨烯材料未来的空气净化应用前景作出了展望。

电加热石墨烯薄膜材料的制备及应用研究进展

介绍了制备低缺陷的电加热石墨烯薄膜材料的几种方法,以及由不同方法得到的石墨烯材料在制备成膜时所采用的不同的成膜技术及其应用,并且分析了不同的方法在大批量制备过程中亟待解决的问题。指出在考虑到低成本大批量制备高性能的电加热石墨烯薄膜材料时,超临界流体剥离法是一种环保无VOC的制备方法,将得到的石墨烯制成浆料可以突破基底的限制而被广泛应用。