PZT nanocrystalline powder was prepared by a stearic acid gel method. Thecrystallization process from the precursor was monitored by infrared spectroscopy, differentialthermal analysis, and thermogravimetric analysis....PZT nanocrystalline powder was prepared by a stearic acid gel method. Thecrystallization process from the precursor was monitored by infrared spectroscopy, differentialthermal analysis, and thermogravimetric analysis. The nano-sized PZT powder was characterized byX-ray diffraction and transmission electron microscopy. It shows that pure single-phase PZT powdercould be obtained at 450 deg C for 1 h, and the particle size is about 20 nm. With an increase inthe calcination temperature, the PZT crystallite size increased.展开更多
基金This work was financially supported by the Ministry of Science and Technology of China through 973-project (No. 2002CB613301).
文摘PZT nanocrystalline powder was prepared by a stearic acid gel method. Thecrystallization process from the precursor was monitored by infrared spectroscopy, differentialthermal analysis, and thermogravimetric analysis. The nano-sized PZT powder was characterized byX-ray diffraction and transmission electron microscopy. It shows that pure single-phase PZT powdercould be obtained at 450 deg C for 1 h, and the particle size is about 20 nm. With an increase inthe calcination temperature, the PZT crystallite size increased.