The effect of mechanical activation on the granulometric parameters,microstructure,and leaching efficiency of chalcopyrite was evaluated,and the occurrence/transition of agglomeration and aggregation was discussed.The...The effect of mechanical activation on the granulometric parameters,microstructure,and leaching efficiency of chalcopyrite was evaluated,and the occurrence/transition of agglomeration and aggregation was discussed.The results showed that in 8 h of milling treatment,the agglomeration and the microstructure did not affect each other.However,with prolonging milling time,the crystallite size tended to reach a saturation value,and the stagnating microstructural changes led to the replacement of agglomeration by aggregation.The leaching results indicated that the mechanical activation can strongly enhance the reactivity of chalcopyrite and the hindering effect of aggregation on leaching was considerably greater than that of agglomeration.Consequently,after 8 h of milling,the maximum Cu leaching rate of 80.13%was achieved after 4 h of acid leaching.展开更多
Mechanical activation(MA) of malachite was carried out by dry planetary grinding(DPG) and wet Isa grinding(WIG) methods. When the rotational speed was increased to 400 r/min in DPG, the specific surface area of malach...Mechanical activation(MA) of malachite was carried out by dry planetary grinding(DPG) and wet Isa grinding(WIG) methods. When the rotational speed was increased to 400 r/min in DPG, the specific surface area of malachite reached the maximum and the particle size reached the minimum of 0.7–100 μm. Agglomeration occurred between mineral particles when the rotational speed was increased to 580 r/min in DPG.However, no agglomeration was observed among particles with sizes 0.4–3 μm in WIG. X-ray diffraction analysis showed that, at a 580 r/min rotational speed in DPG, the amorphization degree of malachite was 53.12%, whereas that in WIG was 71.40%, indicating that MA led to amorphization and distortion of crystal structures. In addition, in the Fourier transform infrared(FT-IR) spectra of activated malachite, the bands associated with –OH, CO_3^(2-)and metal lattice vibrations of Cu–O and Cu–OH were weakened, and a new H–O–H bending mode and peaks of gaseous CO_2 appeared, indicating that MA decreased the band energy, enhanced dihydroxylation, and increased the chemical reactivity of the malachite.Furthermore, the leaching behavior of copper ore was greatly improved by MA.展开更多
The effect of temperature on leaching behavior of copper minerals with different occurrence states in complex copper oxide ores was carried out by phase analysis means of XRD, optical microscopy and SEM-EDS. The resul...The effect of temperature on leaching behavior of copper minerals with different occurrence states in complex copper oxide ores was carried out by phase analysis means of XRD, optical microscopy and SEM-EDS. The results indicated that at ambient temperature, the easily leached copper oxide minerals were completely dissolved, while the bonded copper minerals were insoluble. At lukewarm temperature of 40℃, it was mainly the dissolution of copper in isomorphism state. With increasing temperature to 60℃, the copper leaching rate in the adsorbed state was significantly accelerated. In addition, when the temperature increased to 80℃, the isomorphic copper was completely leached, leaving 11.2% adsorbed copper un-leached. However, the copper in feldspar-quartz-copper-iron colloid state was not dissolved throughout the leaching process. Overall, the leaching rates of copper in different copper minerals decreased in the order: malachite, pseudo-malachite > chrysocolla > copper-bearing chlorite > copper-bearing muscovite > copper-bearing biotite > copper-bearing limonite > feldspar-quartz-copper-iron colloid.展开更多
基金the Special Fund for the National Natural Science Foundation of China(U1608254)the National Key R&D Program of China(2018YFC1902002).
文摘The effect of mechanical activation on the granulometric parameters,microstructure,and leaching efficiency of chalcopyrite was evaluated,and the occurrence/transition of agglomeration and aggregation was discussed.The results showed that in 8 h of milling treatment,the agglomeration and the microstructure did not affect each other.However,with prolonging milling time,the crystallite size tended to reach a saturation value,and the stagnating microstructural changes led to the replacement of agglomeration by aggregation.The leaching results indicated that the mechanical activation can strongly enhance the reactivity of chalcopyrite and the hindering effect of aggregation on leaching was considerably greater than that of agglomeration.Consequently,after 8 h of milling,the maximum Cu leaching rate of 80.13%was achieved after 4 h of acid leaching.
基金financially supported by the Special Funds for the National Natural Science Foundation of China(No.U1608254)the National Key R&D Program of China(No.2018YFC1902002)
文摘Mechanical activation(MA) of malachite was carried out by dry planetary grinding(DPG) and wet Isa grinding(WIG) methods. When the rotational speed was increased to 400 r/min in DPG, the specific surface area of malachite reached the maximum and the particle size reached the minimum of 0.7–100 μm. Agglomeration occurred between mineral particles when the rotational speed was increased to 580 r/min in DPG.However, no agglomeration was observed among particles with sizes 0.4–3 μm in WIG. X-ray diffraction analysis showed that, at a 580 r/min rotational speed in DPG, the amorphization degree of malachite was 53.12%, whereas that in WIG was 71.40%, indicating that MA led to amorphization and distortion of crystal structures. In addition, in the Fourier transform infrared(FT-IR) spectra of activated malachite, the bands associated with –OH, CO_3^(2-)and metal lattice vibrations of Cu–O and Cu–OH were weakened, and a new H–O–H bending mode and peaks of gaseous CO_2 appeared, indicating that MA decreased the band energy, enhanced dihydroxylation, and increased the chemical reactivity of the malachite.Furthermore, the leaching behavior of copper ore was greatly improved by MA.
基金Project(U1608254) supported by the Special Fund for the National Natural Science Foundation of ChinaProjects(ZJKY2017(B)KFJJ01,ZJKY2017(B)KFJJ02) supported by Zijin Mining Group Co.,Ltd.,China
文摘The effect of temperature on leaching behavior of copper minerals with different occurrence states in complex copper oxide ores was carried out by phase analysis means of XRD, optical microscopy and SEM-EDS. The results indicated that at ambient temperature, the easily leached copper oxide minerals were completely dissolved, while the bonded copper minerals were insoluble. At lukewarm temperature of 40℃, it was mainly the dissolution of copper in isomorphism state. With increasing temperature to 60℃, the copper leaching rate in the adsorbed state was significantly accelerated. In addition, when the temperature increased to 80℃, the isomorphic copper was completely leached, leaving 11.2% adsorbed copper un-leached. However, the copper in feldspar-quartz-copper-iron colloid state was not dissolved throughout the leaching process. Overall, the leaching rates of copper in different copper minerals decreased in the order: malachite, pseudo-malachite > chrysocolla > copper-bearing chlorite > copper-bearing muscovite > copper-bearing biotite > copper-bearing limonite > feldspar-quartz-copper-iron colloid.