A novel method to prepare mesoporous nano-zirconia was developed. Thesynthesis was carried out in the presence of PEO surfactants via a solid-state reaction. Thematerials exhibit a strong diffraction peak at low 2θ a...A novel method to prepare mesoporous nano-zirconia was developed. Thesynthesis was carried out in the presence of PEO surfactants via a solid-state reaction. Thematerials exhibit a strong diffraction peak at low 2θ angle and their nitrogenadsorption/desorption isotherms are typical of type IV with H1 hysteresis loops. The pore structureimaged by TEM can be described as wormhole domains. The tetragonal zirconia nanocrystals are uniformin size (around 1.5 nm) and their mesopores focus on around 4.6 nm. The zirconia nanocrystal growthis tentatively postulated to be the result of an aggregation mechanism. This study also revealsthat the PEO surfactants can interact with the Zr-O-Zr framework to reinforce the thermal stabilityof zirconia. The ratio of NaOH to ZrOCl_2, crystallization and calcination temperature play animportant role in the synthesis of mesoporous nano-zirconia.展开更多
文摘A novel method to prepare mesoporous nano-zirconia was developed. Thesynthesis was carried out in the presence of PEO surfactants via a solid-state reaction. Thematerials exhibit a strong diffraction peak at low 2θ angle and their nitrogenadsorption/desorption isotherms are typical of type IV with H1 hysteresis loops. The pore structureimaged by TEM can be described as wormhole domains. The tetragonal zirconia nanocrystals are uniformin size (around 1.5 nm) and their mesopores focus on around 4.6 nm. The zirconia nanocrystal growthis tentatively postulated to be the result of an aggregation mechanism. This study also revealsthat the PEO surfactants can interact with the Zr-O-Zr framework to reinforce the thermal stabilityof zirconia. The ratio of NaOH to ZrOCl_2, crystallization and calcination temperature play animportant role in the synthesis of mesoporous nano-zirconia.