The effects of AITi5B1 grain refinement and cooling rate on the microstructure and mechanical properties of a secondary AlSi7Cu3Mg alloy were reported. Metallographic and image analysis techniques have been used to qu...The effects of AITi5B1 grain refinement and cooling rate on the microstructure and mechanical properties of a secondary AlSi7Cu3Mg alloy were reported. Metallographic and image analysis techniques have been used to quantitatively examine the macrostructural and microstructural changes occurring with the addition of grain-refining agent at different cooling rates by using a step casting die. The results indicate that the addition of AlTi5B1 produces a fine and uniform grain structure throughout the casting and this effect is more pronounced in the slowly solidified regions. Increasing the cooling rate, lower amount of grain refiner is necessary to produce a uniform grain size throughout the casting. On the other hand, the initial contents of Ti and B, present as impurity elements in the supplied secondary alloy, are not sufficient to produce an effective grain refinement. The results from the step casting geometry were applied to investigate a gasoline 16V cylinder head, which was produced by gravity semi-permanent mould technology. The grain refinement improves the plastic behaviour of the alloy and increases the reliability of the casting, as evidenced by the Weibull statistics.展开更多
The effects of Sr addition and pressure increase on the microstructure and casting defects of a low-pressure die cast （LPDC） AISi7Mg0.3 alloy have been studied. Metallographic and image analysis techniques have been...The effects of Sr addition and pressure increase on the microstructure and casting defects of a low-pressure die cast （LPDC） AISi7Mg0.3 alloy have been studied. Metallographic and image analysis techniques have been used to quantitatively examine the microstructural changes and the amount of porosity occurring at different Sr levels and pressure parameters. The results indicate that an increase in the filling pressure induces lower heat dissipation of the liquid close to the die/core surfaces, with the formation of slightly greater dendrite arms and coarser eutectic Si particles. On the other hand, the increase in the Sr level leads to finer microstructural scale and eutectic Si. The analysed variables, within the experimental conditions, do not affect the morphology of eutectic Si particles. Higher applied pressure and Sr content generate castings with lower amount of porosiW. However, as the filling pressure increases the flow of metal inside the die cavity is more turbulent, leading to the formation of oxide films and cold shots. In the analysed range of experimental conditions, the design of experiment methodology and the analysis of variance have been used to develop statistical models that accurately predict the average size of secondary dendrite arm spacing and the amount of porosity in the low-pressure die cast AISiTMg0.3 alloy.展开更多
文摘The effects of AITi5B1 grain refinement and cooling rate on the microstructure and mechanical properties of a secondary AlSi7Cu3Mg alloy were reported. Metallographic and image analysis techniques have been used to quantitatively examine the macrostructural and microstructural changes occurring with the addition of grain-refining agent at different cooling rates by using a step casting die. The results indicate that the addition of AlTi5B1 produces a fine and uniform grain structure throughout the casting and this effect is more pronounced in the slowly solidified regions. Increasing the cooling rate, lower amount of grain refiner is necessary to produce a uniform grain size throughout the casting. On the other hand, the initial contents of Ti and B, present as impurity elements in the supplied secondary alloy, are not sufficient to produce an effective grain refinement. The results from the step casting geometry were applied to investigate a gasoline 16V cylinder head, which was produced by gravity semi-permanent mould technology. The grain refinement improves the plastic behaviour of the alloy and increases the reliability of the casting, as evidenced by the Weibull statistics.
文摘The effects of Sr addition and pressure increase on the microstructure and casting defects of a low-pressure die cast （LPDC） AISi7Mg0.3 alloy have been studied. Metallographic and image analysis techniques have been used to quantitatively examine the microstructural changes and the amount of porosity occurring at different Sr levels and pressure parameters. The results indicate that an increase in the filling pressure induces lower heat dissipation of the liquid close to the die/core surfaces, with the formation of slightly greater dendrite arms and coarser eutectic Si particles. On the other hand, the increase in the Sr level leads to finer microstructural scale and eutectic Si. The analysed variables, within the experimental conditions, do not affect the morphology of eutectic Si particles. Higher applied pressure and Sr content generate castings with lower amount of porosiW. However, as the filling pressure increases the flow of metal inside the die cavity is more turbulent, leading to the formation of oxide films and cold shots. In the analysed range of experimental conditions, the design of experiment methodology and the analysis of variance have been used to develop statistical models that accurately predict the average size of secondary dendrite arm spacing and the amount of porosity in the low-pressure die cast AISiTMg0.3 alloy.
