Grain growth behavior of 5Cr21Mn9Ni4NRE steel was experimentally studied at various solid solution treatment temperatures and holding for different times. The experimental results show that the 5Cr21Mn9Ni4NRE steel ha...Grain growth behavior of 5Cr21Mn9Ni4NRE steel was experimentally studied at various solid solution treatment temperatures and holding for different times. The experimental results show that the 5Cr21Mn9Ni4NRE steel has the feature of sharp austenite grain coarsening after solid solution treatment at the temperature above 1150 ℃. RE added in the steel has the benefit to restrain grain growth and increase grain growth activation energy.展开更多
The oxidation resistance of 5Cr21Mn9Ni4N steel micro-alloying by RE at 700 - 900 ℃ was investigated. The results indicate that oxidation exponent n and oxidation activation energy are increased, and oxidation velocit...The oxidation resistance of 5Cr21Mn9Ni4N steel micro-alloying by RE at 700 - 900 ℃ was investigated. The results indicate that oxidation exponent n and oxidation activation energy are increased, and oxidation velocity constant kp is decreased when 0.2% RE is added in 5Cr21Mn9Ni4N steel. The addition of RE elements does not alter phase constitution of oxidation scale, however it improves the configuration of oxidation scale, and increases thermal stability and adhesivity of oxidation scale, which results in the raise of oxidation resistance of 5Cr21Mn9Ni4N steel at high temperature. The oxidation scale constitutes of refractory steel transfer from manganic oxide mostly to ferric oxide mostly with the increase of temperature, which leads to descend of compactness and desquamation resistance of oxidation scale. The mass increase of ferric oxide in the oxidation scale and the looseness of oxidation scale are the main reason to descend the oxidation resistance of refractory steel.展开更多
文摘Grain growth behavior of 5Cr21Mn9Ni4NRE steel was experimentally studied at various solid solution treatment temperatures and holding for different times. The experimental results show that the 5Cr21Mn9Ni4NRE steel has the feature of sharp austenite grain coarsening after solid solution treatment at the temperature above 1150 ℃. RE added in the steel has the benefit to restrain grain growth and increase grain growth activation energy.
文摘The oxidation resistance of 5Cr21Mn9Ni4N steel micro-alloying by RE at 700 - 900 ℃ was investigated. The results indicate that oxidation exponent n and oxidation activation energy are increased, and oxidation velocity constant kp is decreased when 0.2% RE is added in 5Cr21Mn9Ni4N steel. The addition of RE elements does not alter phase constitution of oxidation scale, however it improves the configuration of oxidation scale, and increases thermal stability and adhesivity of oxidation scale, which results in the raise of oxidation resistance of 5Cr21Mn9Ni4N steel at high temperature. The oxidation scale constitutes of refractory steel transfer from manganic oxide mostly to ferric oxide mostly with the increase of temperature, which leads to descend of compactness and desquamation resistance of oxidation scale. The mass increase of ferric oxide in the oxidation scale and the looseness of oxidation scale are the main reason to descend the oxidation resistance of refractory steel.
