Glass Formation and Thermal Stability in Rapidly Solidified Al-Fe-V-Si Alloy with Misch Metal Additions 被引量:1
1
作者 Wang, JQ Zeng, MG +3 位作者 Tseng, MK Chen, XF Dong, L gu, sx 《Journal of Materials Science & Technology》 SCIE EI CAS CSCD 1996年第1期11-14,共4页
A new amorphous Al(87.3)Fe(4.3)V(0.7)Si(1.7)Mm(6.0)(Mm: misch metal) was prepared by using melt-spinning technique. Differential scanning calorimetry (DSC), X-ray diffraction (XRD), transmission electron microscopy (T... A new amorphous Al(87.3)Fe(4.3)V(0.7)Si(1.7)Mm(6.0)(Mm: misch metal) was prepared by using melt-spinning technique. Differential scanning calorimetry (DSC), X-ray diffraction (XRD), transmission electron microscopy (TEM) and energy dispersive X-ray (EDX) have been used to investigate the crystallization behaviour of this amorphous alloy. It is found that the crystallization process can be concluded as follows: amorphous --> amorphous plus fcc-Al --> fcc-Al plus Al-11(La,Ce)(3) plus i-phase (icosahedral) --> fee-Al plus Al-11(La,Ce)(3) plus i-phase plus ic-phase (icosahedral compounds). The results of microhardness measurement show that HV values are higher than those in AI-Fe-V-Si based alloy, and the maximum HV value corresponds to the coexisting of nanoscale Al particles and i-phase. 展开更多
下载PDF
上一页 1 下一页 到第
使用帮助 返回顶部