ZnS nanoparticles were prepared by using solid-state reaction method at room temperature in agate mortar for the first time. The average particle size was about 20nm. This reaction is affected by the structure of reac...ZnS nanoparticles were prepared by using solid-state reaction method at room temperature in agate mortar for the first time. The average particle size was about 20nm. This reaction is affected by the structure of reactant, crystal water and defects.展开更多
A new type of phosphor Sr2ZrO4 with one-dimensional structure was prepared bysolid reaction and its luminescence is seen at room temperature. The excitation and emissionspectra were measured and display broad maximum ...A new type of phosphor Sr2ZrO4 with one-dimensional structure was prepared bysolid reaction and its luminescence is seen at room temperature. The excitation and emissionspectra were measured and display broad maximum at 354 nm and 386 nm respectively. Themechanism of this luminescence is ascribed to charge transfer.展开更多
The Gd（OH）3 nanorods with diameters of ca. 40--60 nm and lengths of more than 400-550 nm have been prepared by a novel hydrothermal technique. The structural features and chemical composition of the nanorods were in...The Gd（OH）3 nanorods with diameters of ca. 40--60 nm and lengths of more than 400-550 nm have been prepared by a novel hydrothermal technique. The structural features and chemical composition of the nanorods were investigated by X-ray diffraction （XILD）, transmission electron microscopy （TEM）, and field emission scanning electron microscope （FESEM）, selected area electron diffraction （SAED）, and high resolution transmission electron microscopy （HRTEM）. The possible mechanism for the formation of Gd（OH）3 nanorods was proposed.展开更多
La（OH）3 nanorods with diameters of 20-40 nm and lengths of 200-300 nm were synthesized by a hydrothermal microemulsion method. The structure and morphology of the final products were characterized by X-ray powder di...La（OH）3 nanorods with diameters of 20-40 nm and lengths of 200-300 nm were synthesized by a hydrothermal microemulsion method. The structure and morphology of the final products were characterized by X-ray powder diffraction （XRD）, transmission electron microscopy （TEM）, and field emission scanning electron microscope （FESEM）.展开更多
The photochromism in CaS:Sm (from white to pink) was observed for the first time by exposing it to ultraviolet light. The experiments results show that the absorption intensity of Sm2+ in the range of 500 similar to 6...The photochromism in CaS:Sm (from white to pink) was observed for the first time by exposing it to ultraviolet light. The experiments results show that the absorption intensity of Sm2+ in the range of 500 similar to 600nm was strongly increased after irradiation. This reveals that there is the valence changing of Sm. If the sample was excited by visible light again, the pink color turned to white, indicating that CaS:Sm has potential application in the field of storage material.展开更多
文摘ZnS nanoparticles were prepared by using solid-state reaction method at room temperature in agate mortar for the first time. The average particle size was about 20nm. This reaction is affected by the structure of reactant, crystal water and defects.
文摘A new type of phosphor Sr2ZrO4 with one-dimensional structure was prepared bysolid reaction and its luminescence is seen at room temperature. The excitation and emissionspectra were measured and display broad maximum at 354 nm and 386 nm respectively. Themechanism of this luminescence is ascribed to charge transfer.
文摘The Gd（OH）3 nanorods with diameters of ca. 40--60 nm and lengths of more than 400-550 nm have been prepared by a novel hydrothermal technique. The structural features and chemical composition of the nanorods were investigated by X-ray diffraction （XILD）, transmission electron microscopy （TEM）, and field emission scanning electron microscope （FESEM）, selected area electron diffraction （SAED）, and high resolution transmission electron microscopy （HRTEM）. The possible mechanism for the formation of Gd（OH）3 nanorods was proposed.
文摘La（OH）3 nanorods with diameters of 20-40 nm and lengths of 200-300 nm were synthesized by a hydrothermal microemulsion method. The structure and morphology of the final products were characterized by X-ray powder diffraction （XRD）, transmission electron microscopy （TEM）, and field emission scanning electron microscope （FESEM）.
文摘The photochromism in CaS:Sm (from white to pink) was observed for the first time by exposing it to ultraviolet light. The experiments results show that the absorption intensity of Sm2+ in the range of 500 similar to 600nm was strongly increased after irradiation. This reveals that there is the valence changing of Sm. If the sample was excited by visible light again, the pink color turned to white, indicating that CaS:Sm has potential application in the field of storage material.