The effects of calcined lead--zirconate-titanate(PZT)powders on the electric properties of PZT/polyvinylidene-tifluorethylene copolymer(PVDF-TrFE)composites thick films were studied in this paper.Firstly,the PZT powde...The effects of calcined lead--zirconate-titanate(PZT)powders on the electric properties of PZT/polyvinylidene-tifluorethylene copolymer(PVDF-TrFE)composites thick films were studied in this paper.Firstly,the PZT powders synthesized by hydrothermal method were calcined at different temperatures ranging from 300℃ to 900℃,and then the PZT/PVDF-TrFE composites films were produced by casting PZT/PVDF-TrFE suspension onto the indium-tin-oxide(ITO)-coated glass substrates.Electric properties,including dielectric and pyroelectric performances of thick films consisting of PZT powders calcined at different temperatures were tested.The highest pyroelectric cofficient obtained in the sample using 700℃ calcined PZT powders was 96μCm^(-2)K^(-1),which was 20%higher than the composites made of uncalcined powders.Additionally,the highest detectivity figure-of merit(FOM)(FD)of the composite was 1.36×10^(-5)Pa^(-1/2),which increased about 13.5%compared to the one using uncalcined powders.展开更多
基金supported by the National Natural Science Foundation of China(NSFC.51102037)the Fundamental Research Funds for the Central Universities from UESTC(No.ZYGX2010J030 and No.ZYGX2011J023).
文摘The effects of calcined lead--zirconate-titanate(PZT)powders on the electric properties of PZT/polyvinylidene-tifluorethylene copolymer(PVDF-TrFE)composites thick films were studied in this paper.Firstly,the PZT powders synthesized by hydrothermal method were calcined at different temperatures ranging from 300℃ to 900℃,and then the PZT/PVDF-TrFE composites films were produced by casting PZT/PVDF-TrFE suspension onto the indium-tin-oxide(ITO)-coated glass substrates.Electric properties,including dielectric and pyroelectric performances of thick films consisting of PZT powders calcined at different temperatures were tested.The highest pyroelectric cofficient obtained in the sample using 700℃ calcined PZT powders was 96μCm^(-2)K^(-1),which was 20%higher than the composites made of uncalcined powders.Additionally,the highest detectivity figure-of merit(FOM)(FD)of the composite was 1.36×10^(-5)Pa^(-1/2),which increased about 13.5%compared to the one using uncalcined powders.