Mg−1Mn−0.5Al−0.5Ca−0.5Zn(wt.%)alloy was fabricated by conventional extrusion at 673 K with an extrusion ratio of 25:1,followed by aging at 473 K.The microstructure was characterized by scanning electron microscopy,ele...Mg−1Mn−0.5Al−0.5Ca−0.5Zn(wt.%)alloy was fabricated by conventional extrusion at 673 K with an extrusion ratio of 25:1,followed by aging at 473 K.The microstructure was characterized by scanning electron microscopy,electron back-scattered diffraction,and transmission electron microscopy.The mechanical properties were determined by the tensile test.The peak-aged sample shows fine recrystallized grains with an average grain size of 1.7μm.Area fraction of Al−Ca particles in the alloy increases significantly after peak aging.Meanwhile,botháañandác+añdislocations were observed to remain in the alloy after hot extrusion.Thus,the peak-aged sample exhibits simultaneously high strength and good ductility with the ultimate tensile stress,tensile yield stress,and tension fracture elongation of 320 MPa,314 MPa,and 19.0%,respectively.展开更多
基金the financial supports from the Fundamental Research Funds for the Central Universities,China(Nos.2019CDCGCL316,2020CDJDPT001)Chongqing Research Program of Basic Research and Frontier Technology,China(No.cstc2019jcjy-msxmX0539)。
文摘Mg−1Mn−0.5Al−0.5Ca−0.5Zn(wt.%)alloy was fabricated by conventional extrusion at 673 K with an extrusion ratio of 25:1,followed by aging at 473 K.The microstructure was characterized by scanning electron microscopy,electron back-scattered diffraction,and transmission electron microscopy.The mechanical properties were determined by the tensile test.The peak-aged sample shows fine recrystallized grains with an average grain size of 1.7μm.Area fraction of Al−Ca particles in the alloy increases significantly after peak aging.Meanwhile,botháañandác+añdislocations were observed to remain in the alloy after hot extrusion.Thus,the peak-aged sample exhibits simultaneously high strength and good ductility with the ultimate tensile stress,tensile yield stress,and tension fracture elongation of 320 MPa,314 MPa,and 19.0%,respectively.