In the present study, impulse pressuring diffu- sion bonding technology （IPDB） was utilized between commercially pure titanium and 304 stainless steel （SS） using pure nickel （Ni） as interlayer metal. The interfa...In the present study, impulse pressuring diffu- sion bonding technology （IPDB） was utilized between commercially pure titanium and 304 stainless steel （SS） using pure nickel （Ni） as interlayer metal. The interfacial microstructures of the bonded joints were investigated by scanning electron microscopy （SEM） and energy dispersive spectroscope （EDS） analyses. It is found that with the aid of the Ni interlayer, the interdiffusion and reaction between Ti and SS can be effectively restricted and robust joints can be obtained. Intermetallic compounds （IMCs） including Ti2Ni, TiNi, and TiNi3 are detected at the Ti/Ni interface; however, only Ni-Fe solid solution is found at the Ni/SS interface. The maximum tensile strength of 358 MPa is obtained by IPDB for 90 s and the fracture takes place along the Ti2Ni and TiNi phase upon tensile loading. The existence of cleavage pattern on the fracture surface indi- cates the brittle nature of the joints.展开更多
Multiple precipitating species in a 2.2 GPa grade precipitation-hardened martensitic stainless steel with balanced ductility were characterized at atomic scale by atom probe tomography.The results indicated that the c...Multiple precipitating species in a 2.2 GPa grade precipitation-hardened martensitic stainless steel with balanced ductility were characterized at atomic scale by atom probe tomography.The results indicated that the clustering of solute atoms was promoted with progressive aging treatments.(Cr,Mo)-rich carbide(M_(2)C)precipitated at the linear dislocations in the as-aged steels.Obvious segregation of Cr,Mo,and C at phase boundaries favored the precipitation of carbide and caused the formation of Cr-lean domains.Spinodal decomposition of martensitic matrix during aging led to the substantial precipitation of fine Cr-rich(α′Cr)phase.Compared with the first aging treated samples,a synergistic enhancement of both strength and ductility of the secondary aging treated(SAT)samples was primarily ascribed to the enhanced precipitation of Cr-rich phase.Additionally,Ni-rich filmy reversed austenite precipitated at the lath boundary,which was beneficial to the ductility of SAT samples.展开更多
基金financially supported by the National Natural Science Foundation of China(No.50675234)
文摘In the present study, impulse pressuring diffu- sion bonding technology （IPDB） was utilized between commercially pure titanium and 304 stainless steel （SS） using pure nickel （Ni） as interlayer metal. The interfacial microstructures of the bonded joints were investigated by scanning electron microscopy （SEM） and energy dispersive spectroscope （EDS） analyses. It is found that with the aid of the Ni interlayer, the interdiffusion and reaction between Ti and SS can be effectively restricted and robust joints can be obtained. Intermetallic compounds （IMCs） including Ti2Ni, TiNi, and TiNi3 are detected at the Ti/Ni interface; however, only Ni-Fe solid solution is found at the Ni/SS interface. The maximum tensile strength of 358 MPa is obtained by IPDB for 90 s and the fracture takes place along the Ti2Ni and TiNi phase upon tensile loading. The existence of cleavage pattern on the fracture surface indi- cates the brittle nature of the joints.
基金This work was financially supported by the National“13th Five-year Plan”high-tech Research and Development Program of China(YE-17T60270B).
文摘Multiple precipitating species in a 2.2 GPa grade precipitation-hardened martensitic stainless steel with balanced ductility were characterized at atomic scale by atom probe tomography.The results indicated that the clustering of solute atoms was promoted with progressive aging treatments.(Cr,Mo)-rich carbide(M_(2)C)precipitated at the linear dislocations in the as-aged steels.Obvious segregation of Cr,Mo,and C at phase boundaries favored the precipitation of carbide and caused the formation of Cr-lean domains.Spinodal decomposition of martensitic matrix during aging led to the substantial precipitation of fine Cr-rich(α′Cr)phase.Compared with the first aging treated samples,a synergistic enhancement of both strength and ductility of the secondary aging treated(SAT)samples was primarily ascribed to the enhanced precipitation of Cr-rich phase.Additionally,Ni-rich filmy reversed austenite precipitated at the lath boundary,which was beneficial to the ductility of SAT samples.