The effect of F,K,and Na on the solid phase reaction of the Baiyunebo iron ore was investigated by differential thermal analysis （DTA） and X-ray diffraction（XRD）.It has been identified that alkaline elements K and...The effect of F,K,and Na on the solid phase reaction of the Baiyunebo iron ore was investigated by differential thermal analysis （DTA） and X-ray diffraction（XRD）.It has been identified that alkaline elements K and Na in the Baiyunebo ore instigate the formation of low melting point compounds Na2SiO3 and Na2O·Fe2O3 and the generation of molten state in the solid phase sintering.Element F in the Baiyunebo ore facilitates the formation of cuspidine compound 3CaO·2SiO2·CaF2 in the solid phase reaction.The cuspidine compound is kept in solid as one of the final products through the entire sintering process due to its high melting point.In the sintering process,CaF2and SiO2 react with CaO first and form 3CaO·2SiO2·CaF2 and 3CaO·2SiO2,so the formation of ferrites,Na2O·Fe2O3,and 2CaO·Fe2O3 is inhibited.展开更多
In order to fill up the deficiency of the theoretical basis about fluoride formation during Bayan Obo iron concentrate roasting process, the thermodynamic conditions of the interactivity between the components of the ...In order to fill up the deficiency of the theoretical basis about fluoride formation during Bayan Obo iron concentrate roasting process, the thermodynamic conditions of the interactivity between the components of the gangue and calcium fluorite were studied by means of thermodynamic calculation, DTA-TG thermal analysis and XRD characterization. The results revealed that KF, NaF and SiF4 （gaseous） could he,formed during the roasting process, and the tendency of the generation of KF is greater than that of NaF or SiF4 in standard state. Besides, the results of roasting experiments showed that the products of KCaCO3 F and KCaF3 formed in the temperature range of 800-1250 ℃and KF appears when the roasting temperature was higher than 1250 ℃ in K2O-CaF2 system. For the Na2O-CaF2 system, the product of NaF appears at temperature higher than 1050 ℃. The formation reaction of gaseous SiF4 with solid phase CaO · SiO2 in SiO2-CaF2 system took place＂only＇at temperature higher than 1 150 ℃. In the natural potash feldspar-CaF2-CaO system, the fluorination reaction products involved KF at temperature higher than 1 270 ℃ , while in the natural aegirine-CaF2-CaO system, NaF formed at terhperature higher than 980 ℃ during roasting process.展开更多
基金supported by the National Natural Science Foundation of China(No.50664006)
文摘The effect of F,K,and Na on the solid phase reaction of the Baiyunebo iron ore was investigated by differential thermal analysis （DTA） and X-ray diffraction（XRD）.It has been identified that alkaline elements K and Na in the Baiyunebo ore instigate the formation of low melting point compounds Na2SiO3 and Na2O·Fe2O3 and the generation of molten state in the solid phase sintering.Element F in the Baiyunebo ore facilitates the formation of cuspidine compound 3CaO·2SiO2·CaF2 in the solid phase reaction.The cuspidine compound is kept in solid as one of the final products through the entire sintering process due to its high melting point.In the sintering process,CaF2and SiO2 react with CaO first and form 3CaO·2SiO2·CaF2 and 3CaO·2SiO2,so the formation of ferrites,Na2O·Fe2O3,and 2CaO·Fe2O3 is inhibited.
基金Item Sponsored by National Natural Science Foundation of China(51104088)University Science Research Project of Inner Mongolia of China(NJZZ157)
文摘In order to fill up the deficiency of the theoretical basis about fluoride formation during Bayan Obo iron concentrate roasting process, the thermodynamic conditions of the interactivity between the components of the gangue and calcium fluorite were studied by means of thermodynamic calculation, DTA-TG thermal analysis and XRD characterization. The results revealed that KF, NaF and SiF4 （gaseous） could he,formed during the roasting process, and the tendency of the generation of KF is greater than that of NaF or SiF4 in standard state. Besides, the results of roasting experiments showed that the products of KCaCO3 F and KCaF3 formed in the temperature range of 800-1250 ℃and KF appears when the roasting temperature was higher than 1250 ℃ in K2O-CaF2 system. For the Na2O-CaF2 system, the product of NaF appears at temperature higher than 1050 ℃. The formation reaction of gaseous SiF4 with solid phase CaO · SiO2 in SiO2-CaF2 system took place＂only＇at temperature higher than 1 150 ℃. In the natural potash feldspar-CaF2-CaO system, the fluorination reaction products involved KF at temperature higher than 1 270 ℃ , while in the natural aegirine-CaF2-CaO system, NaF formed at terhperature higher than 980 ℃ during roasting process.