Rapidly solidified 2024 aluminium alloy powders were mechanically milled, then consolidated to bulk form. The microstructural changes of the powders in mechanical milling (MM) and consolidation process were characteri...Rapidly solidified 2024 aluminium alloy powders were mechanically milled, then consolidated to bulk form. The microstructural changes of the powders in mechanical milling (MM) and consolidation process were characterized by X-ray diffraction analyses and transmission electron microscopy observations. The results showed that mechanical milling reduced the grain size to nanometer, dissolved the Al2Cu intermetallic compound into the aluminium matrix and produced an aluminium supersaturated solid solution. During consolidation process. the grain size increased to submicrometer, and the Al2Cu and Al2(Cu, Mg, Si, Fe, Mn) compounds precipitated owing to heating. Increasing consolidation temperature and time results in obvious grain growth and coarsening of second phase particles. The tensile yield strength of the consolidated alloy with submicrometer size grains increases with decreasing grain size, and it follows the famous HallPetch relation展开更多
Al-4.9 Fe-4.9 Ni alloy powders have been synthesized by mechanical alloying. The rnechanically alloyed powders are consolidated by hot hydrostatic extrusion. The results show that extrusion tempereture. extrusion rati...Al-4.9 Fe-4.9 Ni alloy powders have been synthesized by mechanical alloying. The rnechanically alloyed powders are consolidated by hot hydrostatic extrusion. The results show that extrusion tempereture. extrusion ratio and lubricant have great effects on the quality of extruded rods and their mechanical properties, The mixture of graphite and glass powders as lubricant can prevent the oxidization of cold compacted billet by cladding the billet with this lubricant before heating. This technique greatly simplifies the conventional densification process of powders展开更多
文摘Rapidly solidified 2024 aluminium alloy powders were mechanically milled, then consolidated to bulk form. The microstructural changes of the powders in mechanical milling (MM) and consolidation process were characterized by X-ray diffraction analyses and transmission electron microscopy observations. The results showed that mechanical milling reduced the grain size to nanometer, dissolved the Al2Cu intermetallic compound into the aluminium matrix and produced an aluminium supersaturated solid solution. During consolidation process. the grain size increased to submicrometer, and the Al2Cu and Al2(Cu, Mg, Si, Fe, Mn) compounds precipitated owing to heating. Increasing consolidation temperature and time results in obvious grain growth and coarsening of second phase particles. The tensile yield strength of the consolidated alloy with submicrometer size grains increases with decreasing grain size, and it follows the famous HallPetch relation
文摘Al-4.9 Fe-4.9 Ni alloy powders have been synthesized by mechanical alloying. The rnechanically alloyed powders are consolidated by hot hydrostatic extrusion. The results show that extrusion tempereture. extrusion ratio and lubricant have great effects on the quality of extruded rods and their mechanical properties, The mixture of graphite and glass powders as lubricant can prevent the oxidization of cold compacted billet by cladding the billet with this lubricant before heating. This technique greatly simplifies the conventional densification process of powders