Ferromagnetic resonance （FMR）, Ferromagnetic antirresonance （FMAR） and low field magnetoimpedance （MI） are the characteristic features of high frequency losses in applied fields. While some results on FMR and FM...Ferromagnetic resonance （FMR）, Ferromagnetic antirresonance （FMAR） and low field magnetoimpedance （MI） are the characteristic features of high frequency losses in applied fields. While some results on FMR and FMAR in CoFeNi electroplated wires were reported earlier, here we present microwave absorption in CuBe wires electroplated by 1 μm FeCoNi magnetic layer at very low fields. These data are comparatively analysed together with longitudinal hysteresis loops in order to reveal the correlation between power absorption and magnetization processes. Microwave studies are made by using the cavity perturbation method at 9.65 GHz for a DC field parallel to the sample axis, and with microwave magnetic field hrf parallel or perpendicular to the wire axis. Two peaks have been observed in all samples, one is due to FMR, and the other is, at very low fields, related to MI. The MI peaks represent minima in power absorption. By comparing with the hysteresis loop we remark the close correspondence between the MI phenomena in the axial mode and the concomitant magnetization process.展开更多
The very high (up to 820% of the magnetoimpedance ratio) and sensitive nonlinear giant magnetoimpedance effect has been studied in the FeCo1Ni magnetic tubes electroplated onto Cu(3%)Be nonmagnetic wirefor frequencies...The very high (up to 820% of the magnetoimpedance ratio) and sensitive nonlinear giant magnetoimpedance effect has been studied in the FeCo1Ni magnetic tubes electroplated onto Cu(3%)Be nonmagnetic wirefor frequencies from 1-10MHz. Special annealing was carried out in order to induce the magnetic anisotropy. The high harmonic generation was observed and the harmonics show larger variations with the external magnetic field than the fundamental frequency. The super high sensitivity of the harmonics is promising as regards the increase of the sensitivity of magnetoimpedance sensors.展开更多
文摘Ferromagnetic resonance （FMR）, Ferromagnetic antirresonance （FMAR） and low field magnetoimpedance （MI） are the characteristic features of high frequency losses in applied fields. While some results on FMR and FMAR in CoFeNi electroplated wires were reported earlier, here we present microwave absorption in CuBe wires electroplated by 1 μm FeCoNi magnetic layer at very low fields. These data are comparatively analysed together with longitudinal hysteresis loops in order to reveal the correlation between power absorption and magnetization processes. Microwave studies are made by using the cavity perturbation method at 9.65 GHz for a DC field parallel to the sample axis, and with microwave magnetic field hrf parallel or perpendicular to the wire axis. Two peaks have been observed in all samples, one is due to FMR, and the other is, at very low fields, related to MI. The MI peaks represent minima in power absorption. By comparing with the hysteresis loop we remark the close correspondence between the MI phenomena in the axial mode and the concomitant magnetization process.
文摘The very high (up to 820% of the magnetoimpedance ratio) and sensitive nonlinear giant magnetoimpedance effect has been studied in the FeCo1Ni magnetic tubes electroplated onto Cu(3%)Be nonmagnetic wirefor frequencies from 1-10MHz. Special annealing was carried out in order to induce the magnetic anisotropy. The high harmonic generation was observed and the harmonics show larger variations with the external magnetic field than the fundamental frequency. The super high sensitivity of the harmonics is promising as regards the increase of the sensitivity of magnetoimpedance sensors.
