This study focuses on the insert-injection molding process. The thermoset composite inserts in this study were carbon fiber/epoxy (CF/Epoxy) prepreg sheets. The injected molded part was glass fiber contained phenolic ...This study focuses on the insert-injection molding process. The thermoset composite inserts in this study were carbon fiber/epoxy (CF/Epoxy) prepreg sheets. The injected molded part was glass fiber contained phenolic resin (GF/PF). The CF/Epoxy was placed in the mold cavity prior to injecting GF/PF onto the inserted injection molded CF/Epoxy specimens. The role of adhesion between the inserted part and injected resin on the mechanical properties was evaluated by 3 point bending and impact tests. In addition, the effect of prepreg orientation on the mechanical properties of the prepreg inserted-injection molding system was investigated. It was found that the prepreg with unidirectional orientation significantly improved flexural and impact strength of the inserted injection molding composites, providing better support and resistance to bending and impact loading. The main failure modes of the specimens were structural and adhesive failure.展开更多
In this paper, woven fabrics of glass fiber/carbon fiber intra-hybrid in plain structure were used to fabricate fiber reinforced plastic (FRP) composite by hand lay-up method. The investigation on tensile property was...In this paper, woven fabrics of glass fiber/carbon fiber intra-hybrid in plain structure were used to fabricate fiber reinforced plastic (FRP) composite by hand lay-up method. The investigation on tensile property was carried out on specimens in 7 orientations including 0°/5°/15°/75°/85°/90° in previous works. With the specimen parameters and experimental data, FEM model was built by the software of Marc. By combining the experimental results and finite element analysis, the modulus was simulated and calculated at the first stage. Then interfacial stress of the 0 degree and 90 degree was also calculated. By the initial fracture stress data from experiment as well as the simulation value of interfacial strength of 0 and 90 degree, the initial fracture stress of the off-axial specimens wascalculated and predicted. The result shows that the interfacial strength of the glass fiber bundle is higher than that of the carbon fiber bundle in transverse direction. By using the interfacial strength and according to the Von Mises yielding criterion, the initial fracture stress was predicted, which can be a contribution to the design or predict of the material properties.展开更多
A microfabrication process for poly(vinylidene fluoride-trifluoroethylene)(P(VDF-TrFE)) based flexible piezoelectric devices is proposed using heat controlled spin coating and reactive ion etching(RIE) techniques.Dry ...A microfabrication process for poly(vinylidene fluoride-trifluoroethylene)(P(VDF-TrFE)) based flexible piezoelectric devices is proposed using heat controlled spin coating and reactive ion etching(RIE) techniques.Dry etching of P(VDF-TrFE) in CF 4 +O2 plasma is found to be more effective than that using SF 6 +O2 or Ar+O2 feed gas with the same radiofrequency power and pressure conditions.A maximum etching rate of 400 nm/min is obtained using the CF 4 +O2 plasma with an oxygen concentration of 60% at an antenna power of 200 W and a platen power of 20 W.The oxygen atoms and fluorine atoms are found to be responsible for the chemical etching process.Microstructuring of P(VDF-TrFE) with a feature size of 10 m is achieved and the patterned films show a high remanent polarization of 63.6mC/m 2.展开更多
文摘This study focuses on the insert-injection molding process. The thermoset composite inserts in this study were carbon fiber/epoxy (CF/Epoxy) prepreg sheets. The injected molded part was glass fiber contained phenolic resin (GF/PF). The CF/Epoxy was placed in the mold cavity prior to injecting GF/PF onto the inserted injection molded CF/Epoxy specimens. The role of adhesion between the inserted part and injected resin on the mechanical properties was evaluated by 3 point bending and impact tests. In addition, the effect of prepreg orientation on the mechanical properties of the prepreg inserted-injection molding system was investigated. It was found that the prepreg with unidirectional orientation significantly improved flexural and impact strength of the inserted injection molding composites, providing better support and resistance to bending and impact loading. The main failure modes of the specimens were structural and adhesive failure.
文摘In this paper, woven fabrics of glass fiber/carbon fiber intra-hybrid in plain structure were used to fabricate fiber reinforced plastic (FRP) composite by hand lay-up method. The investigation on tensile property was carried out on specimens in 7 orientations including 0°/5°/15°/75°/85°/90° in previous works. With the specimen parameters and experimental data, FEM model was built by the software of Marc. By combining the experimental results and finite element analysis, the modulus was simulated and calculated at the first stage. Then interfacial stress of the 0 degree and 90 degree was also calculated. By the initial fracture stress data from experiment as well as the simulation value of interfacial strength of 0 and 90 degree, the initial fracture stress of the off-axial specimens wascalculated and predicted. The result shows that the interfacial strength of the glass fiber bundle is higher than that of the carbon fiber bundle in transverse direction. By using the interfacial strength and according to the Von Mises yielding criterion, the initial fracture stress was predicted, which can be a contribution to the design or predict of the material properties.
文摘A microfabrication process for poly(vinylidene fluoride-trifluoroethylene)(P(VDF-TrFE)) based flexible piezoelectric devices is proposed using heat controlled spin coating and reactive ion etching(RIE) techniques.Dry etching of P(VDF-TrFE) in CF 4 +O2 plasma is found to be more effective than that using SF 6 +O2 or Ar+O2 feed gas with the same radiofrequency power and pressure conditions.A maximum etching rate of 400 nm/min is obtained using the CF 4 +O2 plasma with an oxygen concentration of 60% at an antenna power of 200 W and a platen power of 20 W.The oxygen atoms and fluorine atoms are found to be responsible for the chemical etching process.Microstructuring of P(VDF-TrFE) with a feature size of 10 m is achieved and the patterned films show a high remanent polarization of 63.6mC/m 2.