Type Ib diamonds were grown by the temperature gradient method (TGM) at 5.5 GPa and 1500-1560 K in a china-type cubic anvil high pressure apparatus using Ni70Mn25Co5 alloy as solvent/catalyst. The concentration of nit...Type Ib diamonds were grown by the temperature gradient method (TGM) at 5.5 GPa and 1500-1560 K in a china-type cubic anvil high pressure apparatus using Ni70Mn25Co5 alloy as solvent/catalyst. The concentration of nitrogen (CN) in type Ib diamonds synthesized at different synthesis temperatures was measured by a Fourier transform infrared (FTIR) spectrometer. The dependence of CN in diamond on synthesis temperature was studied. For the type Ib diamonds synthesized using Ni70Mn25Co5 as catalyst, its CN decreases along with the increase of synthesis temperature.展开更多
基金Supported by the National Natural Science Foundation of China (Grant Nos. 50572032, 50731006)
文摘Type Ib diamonds were grown by the temperature gradient method (TGM) at 5.5 GPa and 1500-1560 K in a china-type cubic anvil high pressure apparatus using Ni70Mn25Co5 alloy as solvent/catalyst. The concentration of nitrogen (CN) in type Ib diamonds synthesized at different synthesis temperatures was measured by a Fourier transform infrared (FTIR) spectrometer. The dependence of CN in diamond on synthesis temperature was studied. For the type Ib diamonds synthesized using Ni70Mn25Co5 as catalyst, its CN decreases along with the increase of synthesis temperature.