The Fe-based amorphous coatings were produced by air plasma spraying. The as-sprayed coatings were heat-treated at the temperature of 573, 873, and 1 023 K, respectively. The crystallization and wear behavior of the h...The Fe-based amorphous coatings were produced by air plasma spraying. The as-sprayed coatings were heat-treated at the temperature of 573, 873, and 1 023 K, respectively. The crystallization and wear behavior of the heat-treated amorphous coatings were investigated. It was found that the amorphous- nanocrystalline transformation appeared when the as-sprayed coatings were treated at 853 K. The crystallization process had completed and a coating with microcrystallines was formed when the treatment temperature reached 1 023 K. The resultant amorphous and nanocrystalline composite coatings exhibited superior wear resistance compared to crystalline coating. It is attributed to fine grain strengthening of formed nanocrystallines.展开更多
To improve the low thermal conductivities and poor wear resistances of TC4(Ti-6Al-4V)alloy,the most widely used titanium alloy,the surface of TC4 alloys is modified by electroplating deposition of Ni and Cu layers,and...To improve the low thermal conductivities and poor wear resistances of TC4(Ti-6Al-4V)alloy,the most widely used titanium alloy,the surface of TC4 alloys is modified by electroplating deposition of Ni and Cu layers,and then heat-treated to increase the diffusivity at the interface.In this paper,the corrosion behavior of Cu/Ni coatings on TC4 alloy at different heat treatment processes was investigated in 3.5 wt%Na Cl by the electrochemical analysis,and the microstructure and composition of corrosion products was carried out to reveal the corrosion resistance mechanism of Cu/Ni coatings.It was found that the corrosion resistance was significantly influenced by heat treatment temperature.With the increasing diffusion treatment temperature from 500 to 700℃,the corrosion potential positively shifted from-330.87 to-201.14 m V,and the corrosion current density decreased from 4.02×10^-3 to 0.514×10^-3 m A/cm^2.However,when heat treatment temperature increased to 800℃,the corrosion potential negatively shifted to-207.21 m V,and the current density increased to 1.62×10^-3 m A/cm^2.The diffusion behavior of Ti,Ni and Cu elements occurred and small amounts of Ni and Ti elements appeared on the specimen surface under different heat treatment temperature.Especially heattreated at 700℃,the smaller pore size,dense Cu2O film,and highly stable Ti O and Ni O oxide layer were formed,which dramatically enhanced the corrosion resistance of Cu/Ni coatings.Finally,a novel model of corrosion resistance was proposed based on the analysis mentioned above.展开更多
The parameters for the electro-deposition of Cu were optimized in order to increase the compressive properties of close cell aluminum. Different values of deposition voltages and times were considered to vary the amou...The parameters for the electro-deposition of Cu were optimized in order to increase the compressive properties of close cell aluminum. Different values of deposition voltages and times were considered to vary the amount of deposited Cu. The surface morphology of the coating was observed by SEM and the compressive properties were evaluated by MTS. The results show that the coating is more homogeneous and compact with increasing voltage in a certain range, and beyond which, the coating quality decreases apparently. The reason is dedicated to the discharge rate of Cu2+ and nucleus formed in unit time. The compression results show three experienced stages: elastic deformation stage, collapse deformation stage and densification stage. After the electro-deposition of Cu, the elasticity modulus is increased obviously and the platform stress is also increased. Under the same strain, the stress of the aluminum foam with coating is reinforced comparing with the aluminum foam without coating. Furthermore, the platform area is widened apparently. In addition, Cu-SiC nanocomposite coatings are electrodeposited in alumium foams for further improving the mechanical characterization.展开更多
The compound GdNiSn has been studied by X-ray powder diffraction technique.The crystal structure and the X-ray diffraction data for this compound at room temperature are reported.The compound GdNiSn is orthorhombic wi...The compound GdNiSn has been studied by X-ray powder diffraction technique.The crystal structure and the X-ray diffraction data for this compound at room temperature are reported.The compound GdNiSn is orthorhombic with lattice parameters a=7.2044(1)A,b=7.6895(6)A,c=4.4772(4)A,space group Pna2_(1) and 4 formula units of GdNiSn in unit cell.The Smith and Snyder figure of index F_(30) for this compound is 35(0.015,59).展开更多
基金Funded by the Basic Scientific Research of Central Colleges,Chang’an University (No. CHD2011JC126)
文摘The Fe-based amorphous coatings were produced by air plasma spraying. The as-sprayed coatings were heat-treated at the temperature of 573, 873, and 1 023 K, respectively. The crystallization and wear behavior of the heat-treated amorphous coatings were investigated. It was found that the amorphous- nanocrystalline transformation appeared when the as-sprayed coatings were treated at 853 K. The crystallization process had completed and a coating with microcrystallines was formed when the treatment temperature reached 1 023 K. The resultant amorphous and nanocrystalline composite coatings exhibited superior wear resistance compared to crystalline coating. It is attributed to fine grain strengthening of formed nanocrystallines.
基金Funded by Key Projects of Shaanxi Natural Science Foundation(No.2019JZ-27)Shaanxi Natural Science Basic Research Program-Shaanxi Coal(No.2019JLM-47)Fundamental Research Funds for the Central Universities CHD(No.300102319304).
文摘To improve the low thermal conductivities and poor wear resistances of TC4(Ti-6Al-4V)alloy,the most widely used titanium alloy,the surface of TC4 alloys is modified by electroplating deposition of Ni and Cu layers,and then heat-treated to increase the diffusivity at the interface.In this paper,the corrosion behavior of Cu/Ni coatings on TC4 alloy at different heat treatment processes was investigated in 3.5 wt%Na Cl by the electrochemical analysis,and the microstructure and composition of corrosion products was carried out to reveal the corrosion resistance mechanism of Cu/Ni coatings.It was found that the corrosion resistance was significantly influenced by heat treatment temperature.With the increasing diffusion treatment temperature from 500 to 700℃,the corrosion potential positively shifted from-330.87 to-201.14 m V,and the corrosion current density decreased from 4.02×10^-3 to 0.514×10^-3 m A/cm^2.However,when heat treatment temperature increased to 800℃,the corrosion potential negatively shifted to-207.21 m V,and the current density increased to 1.62×10^-3 m A/cm^2.The diffusion behavior of Ti,Ni and Cu elements occurred and small amounts of Ni and Ti elements appeared on the specimen surface under different heat treatment temperature.Especially heattreated at 700℃,the smaller pore size,dense Cu2O film,and highly stable Ti O and Ni O oxide layer were formed,which dramatically enhanced the corrosion resistance of Cu/Ni coatings.Finally,a novel model of corrosion resistance was proposed based on the analysis mentioned above.
基金Funded in Part by the Fundamental Research Funds for the Central Universities(Nos.300102318205,310831161020,310831163401)the National Natural Science Foundation of China(No.51301021)+2 种基金the China Postdoctoral Science Foundation(No.2016M592730)the Innovation and Entrepreneurship Training Program of Chang’an University(No.201610710084)the Fund of the State Key Laboratory of Solidification and Processing in Northwestern Polytechnical University(No.SKLSP201302)
文摘The parameters for the electro-deposition of Cu were optimized in order to increase the compressive properties of close cell aluminum. Different values of deposition voltages and times were considered to vary the amount of deposited Cu. The surface morphology of the coating was observed by SEM and the compressive properties were evaluated by MTS. The results show that the coating is more homogeneous and compact with increasing voltage in a certain range, and beyond which, the coating quality decreases apparently. The reason is dedicated to the discharge rate of Cu2+ and nucleus formed in unit time. The compression results show three experienced stages: elastic deformation stage, collapse deformation stage and densification stage. After the electro-deposition of Cu, the elasticity modulus is increased obviously and the platform stress is also increased. Under the same strain, the stress of the aluminum foam with coating is reinforced comparing with the aluminum foam without coating. Furthermore, the platform area is widened apparently. In addition, Cu-SiC nanocomposite coatings are electrodeposited in alumium foams for further improving the mechanical characterization.
基金Supported by a Grant-in-Aid from the International Centre for Diffraction Data and the Natural Science Foundation of Guangxi Zhuang Autonomous Region。
文摘The compound GdNiSn has been studied by X-ray powder diffraction technique.The crystal structure and the X-ray diffraction data for this compound at room temperature are reported.The compound GdNiSn is orthorhombic with lattice parameters a=7.2044(1)A,b=7.6895(6)A,c=4.4772(4)A,space group Pna2_(1) and 4 formula units of GdNiSn in unit cell.The Smith and Snyder figure of index F_(30) for this compound is 35(0.015,59).