Electroless CoFeB films with good soft magnetic properties were fabricated on polyester plastic substrate from sodium tartarate as a complexing agent.The plating rate of electroless CoFeB films is a function of concen...Electroless CoFeB films with good soft magnetic properties were fabricated on polyester plastic substrate from sodium tartarate as a complexing agent.The plating rate of electroless CoFeB films is a function of concentration of sodium tetrahydroborate,pH of the plating bath,plating temperature and the metallic ratio.The estimated regression coefficient b0-b3 confidence interval,residual error r and confidence interval rint were confirmed by a computer program.The optimal composition of the plating bath was obtained and the dynamic electromagnetic parameters of films were measured in the 2-10 GHz range.At 2 GHz,the μ＇,μ″ of the electroless CoFeB films were 304 and 76.6,respectively,as the concentration of reducer is 1 g/L.Magnetic hysteresis loop of the deposited CoFeB films show a remanence close to the saturation magnetization and coercivity of about 55.7-127.4 A/m.The loops along the hard axis display low anisotropic field Hk of 2 388-3 582 A/m.展开更多
文摘Electroless CoFeB films with good soft magnetic properties were fabricated on polyester plastic substrate from sodium tartarate as a complexing agent.The plating rate of electroless CoFeB films is a function of concentration of sodium tetrahydroborate,pH of the plating bath,plating temperature and the metallic ratio.The estimated regression coefficient b0-b3 confidence interval,residual error r and confidence interval rint were confirmed by a computer program.The optimal composition of the plating bath was obtained and the dynamic electromagnetic parameters of films were measured in the 2-10 GHz range.At 2 GHz,the μ＇,μ″ of the electroless CoFeB films were 304 and 76.6,respectively,as the concentration of reducer is 1 g/L.Magnetic hysteresis loop of the deposited CoFeB films show a remanence close to the saturation magnetization and coercivity of about 55.7-127.4 A/m.The loops along the hard axis display low anisotropic field Hk of 2 388-3 582 A/m.