The corrosion behavior of TP304H steel with combined treatment of shot blasting and electrophoresis deposited RE coating in l%SO2+14%O2+85%Ar mixture gaseous has been studied at 923K for 150 hours. The results show th...The corrosion behavior of TP304H steel with combined treatment of shot blasting and electrophoresis deposited RE coating in l%SO2+14%O2+85%Ar mixture gaseous has been studied at 923K for 150 hours. The results show that both RE coating and shot blasting can improve the corrosion resistance of TP304H steel, and combined treatment has the best effect. Combined treatment reduces 50% mass gain, enhances the continuous and compactness of scale and changes the scale phase forms from FeaOs/Fe^S/Ni^/S to Cr2O3/FeCr2S4/Ni3_xS2. The synergistic effects of combined treatment on corrosion resistance and the effect of shot blasting on corrosion kinetics are discussed. Shot blasting increases the outward diffusion and surface concentration of Cr, Ce coating promotes the selective oxidation of Cr.展开更多
Shot blasting on a tube steel of TP304H can greatly improve the oxidation resistance at *50°C—770°C in water vapor, by the presence of an appropriate blasting intensity. SEM and EPMA analysis indicated that...Shot blasting on a tube steel of TP304H can greatly improve the oxidation resistance at *50°C—770°C in water vapor, by the presence of an appropriate blasting intensity. SEM and EPMA analysis indicated that the structure of the oxide scale turned from multi-layer to monolayer after blasting and Cr2O3 in predominant. The untreated sample characterized in multi-layer oxide was composed of Fe in the outer layer and Fe and Cr underneath. For blasted one, the increase of diffusion rate of Cr and the decrease of effective diffusion energy of scale led to a uniform Cr-rich oxide layer, which was dense and protective and the oxidation resistance was increased.展开更多
文摘The corrosion behavior of TP304H steel with combined treatment of shot blasting and electrophoresis deposited RE coating in l%SO2+14%O2+85%Ar mixture gaseous has been studied at 923K for 150 hours. The results show that both RE coating and shot blasting can improve the corrosion resistance of TP304H steel, and combined treatment has the best effect. Combined treatment reduces 50% mass gain, enhances the continuous and compactness of scale and changes the scale phase forms from FeaOs/Fe^S/Ni^/S to Cr2O3/FeCr2S4/Ni3_xS2. The synergistic effects of combined treatment on corrosion resistance and the effect of shot blasting on corrosion kinetics are discussed. Shot blasting increases the outward diffusion and surface concentration of Cr, Ce coating promotes the selective oxidation of Cr.
文摘Shot blasting on a tube steel of TP304H can greatly improve the oxidation resistance at *50°C—770°C in water vapor, by the presence of an appropriate blasting intensity. SEM and EPMA analysis indicated that the structure of the oxide scale turned from multi-layer to monolayer after blasting and Cr2O3 in predominant. The untreated sample characterized in multi-layer oxide was composed of Fe in the outer layer and Fe and Cr underneath. For blasted one, the increase of diffusion rate of Cr and the decrease of effective diffusion energy of scale led to a uniform Cr-rich oxide layer, which was dense and protective and the oxidation resistance was increased.