The differences of the microstructure and mechanical property between metal mould and sand mould cast Mg-10Gd-3Y-Zr alloy were investigated both under as-cast condition and after solution heat treatment.In the as-cast...The differences of the microstructure and mechanical property between metal mould and sand mould cast Mg-10Gd-3Y-Zr alloy were investigated both under as-cast condition and after solution heat treatment.In the as-cast specimens,the microstructure is similar and composed of α-Mg solid solution and eutectic compound of α-Mg+ Mg24(Gd,Y) 5;whereas the grain size using metal mould and sand mould is 27 μm and 71 μm,respectively.The eutectic compound of metal mould cast alloy was completely dissolved after solution treated at 500℃ for 8 h,however it needs higher temperature(525 ℃) and longer time(12 h) to achieve the absolute dissolving under sand mould condition.In contrast to metal mould,the peak time of sand mould alloy aged at 225 ℃ and 250 ℃ of was advanced by 4 h and 6 h,respectively.The precipitation reaction sequence in sand mould cast Mg-10Gd-3Y-Zr alloy during isothermal ageing at 250 ℃ follows S.S.S.S.→β″(D019) →β'(cboc) →β1(fcc) →β(fcc) ,which is similar to that in the alloy cast using metal mould.展开更多
Ti-based alloys have been widely applied in the aerospace field,owing to their outstanding performance.Precision casting can be used to make integrated near-net-shape components with complex thin-walled structures,whi...Ti-based alloys have been widely applied in the aerospace field,owing to their outstanding performance.Precision casting can be used to make integrated near-net-shape components with complex thin-walled structures,which will further promote the engineering application of Ti-based alloys. In this paper,the research progress of Tibased alloys,e. g.,high-temperature Ti-based alloys,high-strength Ti-based alloys,TiAl-based alloys,Ti-based matrix composites,and their precision casting technologies are reviewed. In addition,the development directions of Tibased alloys are presented based on the application status of Ti-based alloys in the aerospace field.展开更多
Magnesium alloys are well applied in aerospace and aviation because of their mass saving potential,good electromagnetic shielding performance,and high damping capacity. To further promote the applications,in this pape...Magnesium alloys are well applied in aerospace and aviation because of their mass saving potential,good electromagnetic shielding performance,and high damping capacity. To further promote the applications,in this paper,the applications of magnesium alloys are reviewed,which could provide insights for researchers and application designers. Firstly,the applications in aerospace are reviewed,including missile,satellite,rocket,and spacecraft.Secondly,the applications and commercial magnesium alloys in aviation are summarized. Thirdly,the bottleneck and existing problems for such magnesium alloys applied in aerospace and aviation are discussed. The requirements for the magnesium alloy performance in aerospace and aviation are evaluated and elaborated.展开更多
基金funded by the National Basic Research Program of China under contract No.2007CB613701National Key Technology R&D Program of China under contract No.2006BAE04B07-2Program of Shanghai Subject Chief Scientist under contract No.08XD14020
文摘The differences of the microstructure and mechanical property between metal mould and sand mould cast Mg-10Gd-3Y-Zr alloy were investigated both under as-cast condition and after solution heat treatment.In the as-cast specimens,the microstructure is similar and composed of α-Mg solid solution and eutectic compound of α-Mg+ Mg24(Gd,Y) 5;whereas the grain size using metal mould and sand mould is 27 μm and 71 μm,respectively.The eutectic compound of metal mould cast alloy was completely dissolved after solution treated at 500℃ for 8 h,however it needs higher temperature(525 ℃) and longer time(12 h) to achieve the absolute dissolving under sand mould condition.In contrast to metal mould,the peak time of sand mould alloy aged at 225 ℃ and 250 ℃ of was advanced by 4 h and 6 h,respectively.The precipitation reaction sequence in sand mould cast Mg-10Gd-3Y-Zr alloy during isothermal ageing at 250 ℃ follows S.S.S.S.→β″(D019) →β'(cboc) →β1(fcc) →β(fcc) ,which is similar to that in the alloy cast using metal mould.
文摘Ti-based alloys have been widely applied in the aerospace field,owing to their outstanding performance.Precision casting can be used to make integrated near-net-shape components with complex thin-walled structures,which will further promote the engineering application of Ti-based alloys. In this paper,the research progress of Tibased alloys,e. g.,high-temperature Ti-based alloys,high-strength Ti-based alloys,TiAl-based alloys,Ti-based matrix composites,and their precision casting technologies are reviewed. In addition,the development directions of Tibased alloys are presented based on the application status of Ti-based alloys in the aerospace field.
基金the National Natural Science Foundation of China(No. U2037601 and No. 52074183)the Opening Foundation of the National Key Laboratory of Rare Metal Specialty Materials(No. SKL2018K001)the China Scholarship Council(No. 201906230111)。
文摘Magnesium alloys are well applied in aerospace and aviation because of their mass saving potential,good electromagnetic shielding performance,and high damping capacity. To further promote the applications,in this paper,the applications of magnesium alloys are reviewed,which could provide insights for researchers and application designers. Firstly,the applications in aerospace are reviewed,including missile,satellite,rocket,and spacecraft.Secondly,the applications and commercial magnesium alloys in aviation are summarized. Thirdly,the bottleneck and existing problems for such magnesium alloys applied in aerospace and aviation are discussed. The requirements for the magnesium alloy performance in aerospace and aviation are evaluated and elaborated.