CoPt thin films with various Cu contents varying from 0 vol.% to 21.5 vol.% were deposited on glass substrates by magnetron sputtering. The effects of Cu additive on the structural and magnetic properties and the orde...CoPt thin films with various Cu contents varying from 0 vol.% to 21.5 vol.% were deposited on glass substrates by magnetron sputtering. The effects of Cu additive on the structural and magnetic properties and the ordering temperature of CoPt films were investigated in detail. The results show that the Cu in CoPt films plays an important role in promoting the ordering parameter S and reducing the ordering temperature of CoPt films. A nearly perfect （001） texture was obtained in a CoPt film doped with 15.3 vol.% Cu. Besides, the preferred orientation of the CoPt film can be changed by annealing temperature. The perpendicular growth of the CoPt film is favored at a high annealing temperature.展开更多
基金supported by the Natural Science Foundation of China (No. 60776008)the Program for New Century Excellent Talents in Universities, China (No. NECT-07-0527)the Key Project of Chinese Ministry of Education (No. 207020)
文摘CoPt thin films with various Cu contents varying from 0 vol.% to 21.5 vol.% were deposited on glass substrates by magnetron sputtering. The effects of Cu additive on the structural and magnetic properties and the ordering temperature of CoPt films were investigated in detail. The results show that the Cu in CoPt films plays an important role in promoting the ordering parameter S and reducing the ordering temperature of CoPt films. A nearly perfect （001） texture was obtained in a CoPt film doped with 15.3 vol.% Cu. Besides, the preferred orientation of the CoPt film can be changed by annealing temperature. The perpendicular growth of the CoPt film is favored at a high annealing temperature.