Ce-Zr compounds such as Cc0.68Zr0.3202 solid solution, Ce/Zr nitrate and CeO2/ZrO2 were added into γ-alumina-based slurries, which were then loaded on FeCrAl foils pretreated at 950℃ and 1100℃. The microstructures ...Ce-Zr compounds such as Cc0.68Zr0.3202 solid solution, Ce/Zr nitrate and CeO2/ZrO2 were added into γ-alumina-based slurries, which were then loaded on FeCrAl foils pretreated at 950℃ and 1100℃. The microstructures and adhesion performance between the substrates and the washcoats were measured by SEM, BET surface area, ultrasonic vibration and thermal shock test. The results show that the addition of Ce0.68Zr0.32O2 solid solution, Ce/Zr nitrate and CeO2/ZrO2 into the slurries can improve γ-Al2O3-based washcoat adhesion on FeCrAl foils. Furthermore, ceria-zirconia solid solution increases the adhesion of the washcoat on the surface of an FeCrAl foil than the two others. The specific surface area of this washcoat remains about 4345 m^2/g and the weight loss is below 4.0% even after aging test of 10% steam-containing air at 1050℃ for 20 h.展开更多
基金[The work was financially supported by the National Key Basic Research Program of China ("973")(No. 2004CB719503).]
文摘Ce-Zr compounds such as Cc0.68Zr0.3202 solid solution, Ce/Zr nitrate and CeO2/ZrO2 were added into γ-alumina-based slurries, which were then loaded on FeCrAl foils pretreated at 950℃ and 1100℃. The microstructures and adhesion performance between the substrates and the washcoats were measured by SEM, BET surface area, ultrasonic vibration and thermal shock test. The results show that the addition of Ce0.68Zr0.32O2 solid solution, Ce/Zr nitrate and CeO2/ZrO2 into the slurries can improve γ-Al2O3-based washcoat adhesion on FeCrAl foils. Furthermore, ceria-zirconia solid solution increases the adhesion of the washcoat on the surface of an FeCrAl foil than the two others. The specific surface area of this washcoat remains about 4345 m^2/g and the weight loss is below 4.0% even after aging test of 10% steam-containing air at 1050℃ for 20 h.