In this study,a zwitterionic polymer/liquid crystals composite film with programming shape-morphing behavior and humidityresponsive self-healing performance was prepared by blending a zwitterionic polymer and liquid c...In this study,a zwitterionic polymer/liquid crystals composite film with programming shape-morphing behavior and humidityresponsive self-healing performance was prepared by blending a zwitterionic polymer and liquid crystalline azobenzene compound in solution,followed by film-forming in a mold without tedious or multistep synthetic route.The as-obtained zwitterionic polymer/liquid crystal composite film exhibited programming shape-morphing behavior under different stimuli.In this process,the temporary shape of the composite film was memorized after the removal of the stimuli.Such characteristics would fit the requirements of intelligence and energy-saving for stimuliresponsive shape-changing materials.Moreover,the composite film showed humidity-responsive self-healing performances under wet conditions at room temperature.In summary,the simple design and preparation route of the zwitterionic polymer/liquid crystal composite film with programming shape-morphing behavior and mild condition-responsive self-healing performance look promising for the fabrication and practical application of novel photo-driven devices and soft robotics.展开更多
基金the National Natural Science Foundation of China(Nos.51773120 and 51802201)the Guangdong Basic and Applied Basic Research Foundation(No.2022A1515011985)+1 种基金the Shenzhen Science and Technology Planning Project(Nos.JCYJ20190808115609663 and JCYJ20190808123207674)the Scientific Research Project of Guangdong Provincial Department of Education(No.2020ZDZX2040).
文摘In this study,a zwitterionic polymer/liquid crystals composite film with programming shape-morphing behavior and humidityresponsive self-healing performance was prepared by blending a zwitterionic polymer and liquid crystalline azobenzene compound in solution,followed by film-forming in a mold without tedious or multistep synthetic route.The as-obtained zwitterionic polymer/liquid crystal composite film exhibited programming shape-morphing behavior under different stimuli.In this process,the temporary shape of the composite film was memorized after the removal of the stimuli.Such characteristics would fit the requirements of intelligence and energy-saving for stimuliresponsive shape-changing materials.Moreover,the composite film showed humidity-responsive self-healing performances under wet conditions at room temperature.In summary,the simple design and preparation route of the zwitterionic polymer/liquid crystal composite film with programming shape-morphing behavior and mild condition-responsive self-healing performance look promising for the fabrication and practical application of novel photo-driven devices and soft robotics.