A novel Sb2O3/Sb2S3/FeOOH photoanode was fabricated via a simple solution impregnation method along with chemical bath deposition and post-sulfidation.The X-ray diffractometry,Raman measurement,and X-ray photoelectron...A novel Sb2O3/Sb2S3/FeOOH photoanode was fabricated via a simple solution impregnation method along with chemical bath deposition and post-sulfidation.The X-ray diffractometry,Raman measurement,and X-ray photoelectron spectroscopy show that the Sb2O3/Sb2S3/FeOOH thin films are successfully prepared.SEM−EDS analyses reveal that the surface of Sb2O3/Sb2S3 thin films becomes rough after the immersion in the FeCl3 solution.The optimized impregnation time is found to be 8 h.The FeOOH co-catalyst loaded Sb2O3/Sb2S3 electrode exhibits an enhanced photocurrent density of 0.45 mA/cm2 at 1.23 V versus RHE under simulated 1 sun,which is approximately 1.41 times compared to the photocurrent density of the unloaded one.Through the further tests of UV−Vis spectroscopy,the electrochemical impedance spectra,and the PEC measurements,the enhancement can result from the increased light-harvesting ability,the decreased interface transmission impedance,and the remarkably enhanced carrier injection efficiency.展开更多
基金Project(51674298)supported by the National Natural Science Foundation of ChinaProject(2017JJ3384)supported by the Natural Science Foundation of Hunan Province,ChinaProject(2018M630910)supported by the China Postdoctoral Science Foundation。
文摘A novel Sb2O3/Sb2S3/FeOOH photoanode was fabricated via a simple solution impregnation method along with chemical bath deposition and post-sulfidation.The X-ray diffractometry,Raman measurement,and X-ray photoelectron spectroscopy show that the Sb2O3/Sb2S3/FeOOH thin films are successfully prepared.SEM−EDS analyses reveal that the surface of Sb2O3/Sb2S3 thin films becomes rough after the immersion in the FeCl3 solution.The optimized impregnation time is found to be 8 h.The FeOOH co-catalyst loaded Sb2O3/Sb2S3 electrode exhibits an enhanced photocurrent density of 0.45 mA/cm2 at 1.23 V versus RHE under simulated 1 sun,which is approximately 1.41 times compared to the photocurrent density of the unloaded one.Through the further tests of UV−Vis spectroscopy,the electrochemical impedance spectra,and the PEC measurements,the enhancement can result from the increased light-harvesting ability,the decreased interface transmission impedance,and the remarkably enhanced carrier injection efficiency.