A newly designed hot-stamping steel alloyed by chromium （Cr） and manganese （Mn） without boron （B） addition was developed for automobile mass reduction. The experimental results showed the Cr-Mn alloyed steel cou...A newly designed hot-stamping steel alloyed by chromium （Cr） and manganese （Mn） without boron （B） addition was developed for automobile mass reduction. The experimental results showed the Cr-Mn alloyed steel could be quenched to full martensite microstructure when the cooling rate was higher than 14 ℃/s. Yield strength, tensile strength and elongation of the experimental hot stamping part reached 1 180 MPa, 1 645 MPa and 8.4% , respectively. The experimental hot stamping part possessed higher tensile strength and elongation, compared with conventional hot-stamping steel of 22MnB5. Furthermore, excellent processing flexibility would be obtained in this novel hot-stamping steel because of its lower critical cooling rate and phase transformation temperature. The design of the composition and investigations of microstructure, mechanical properties and hot-stamping processing were also studied.展开更多
基金Item Sponsored by Science and Technology Department of Anhui Province of China(12010202015)
文摘A newly designed hot-stamping steel alloyed by chromium （Cr） and manganese （Mn） without boron （B） addition was developed for automobile mass reduction. The experimental results showed the Cr-Mn alloyed steel could be quenched to full martensite microstructure when the cooling rate was higher than 14 ℃/s. Yield strength, tensile strength and elongation of the experimental hot stamping part reached 1 180 MPa, 1 645 MPa and 8.4% , respectively. The experimental hot stamping part possessed higher tensile strength and elongation, compared with conventional hot-stamping steel of 22MnB5. Furthermore, excellent processing flexibility would be obtained in this novel hot-stamping steel because of its lower critical cooling rate and phase transformation temperature. The design of the composition and investigations of microstructure, mechanical properties and hot-stamping processing were also studied.