Understandings of the effect of hot deformation parameters close to the practical production line on grain refinement are crucial for enhancing both the strength and toughness of future rail steels.In this work,the au...Understandings of the effect of hot deformation parameters close to the practical production line on grain refinement are crucial for enhancing both the strength and toughness of future rail steels.In this work,the austenite dynamic recrystallization(DRX)behaviors of a eutectoid pearlite rail steel were studied using a thermo-mechanical simulator with hot deformation parameters frequently employed in rail production lines.The single-pass hot deformation results reveal that the prior austenite grain sizes(PAGSs)for samples with different deformation reductions decrease initially with an increase in deformation temperature.However,once the deformation temperature is beyond a certain threshold,the PAGSs start to increase.It can be attributed to the rise in DRX volume fraction and the increase of DRX grain with deformation temperature,respectively.Three-pass hot deformation results show that the accumulated strain generated in the first and second deformation passes can increase the extent of DRX.In the case of complete DRX,PAGS is predominantly determined by the deformation temperature of the final pass.It suggests a strategic approach during industrial production where part of the deformation reduction in low temperature range can be shifted to the medium temperature range to release rolling mill loads.展开更多
In this paper,dependence of magnetic properties on microstructure and composition of Ce-Fe-B sintered magnets with Cu-doped Ce-rich alloy addition was investigated.It shows that the maximum energy product(BH)(max)and ...In this paper,dependence of magnetic properties on microstructure and composition of Ce-Fe-B sintered magnets with Cu-doped Ce-rich alloy addition was investigated.It shows that the maximum energy product(BH)(max)and coercivity H(cj)of Ce-Fe-B sintered magnet are improved from 6.76 to 9.13 MGOe by 35.1%,and from 1.44 to 1.67 kOe by 16.0%,respectively,via adding 5 wt%liquid phase alloy of Ce(35.58)Fe(57.47)Cu6 B(0.95)(at%).Compared with the magnet without Cerich alloy addition,the volume fraction of the grain-boundary phase with low melting point increases in the magnet with Ce-rich alloy additio n,which is be ne ficial to imp roving the microstructure and promoting the coercivity enhancement of the magnet.In the Ce-Fe-B magnet with Ce-rich alloy addition,Cu and Ce enrich in the grain boundaries of the magnet after annealing,therefore the as-annealed magnet has a higher coercivity than the as-sintered magnet.A distinct Fe-rich layer with the average thickness of 60 nm is found in the grain boundaries in the magnet without Ce-rich alloy addition,but it seems that Fe-rich phase disappears in the magnet with Ce-rich alloy addition.The present work suggests that the further improvement of coercivity in the Ce-Fe-B sintered magnets is expectable by designing the composition and structure of added liquid phase alloys.展开更多
基金financially supported by the National Natural Science Foundation of China(Nos.52293395 and 52293393)the Xiongan Science and Technology Innovation Talent Project of MOST,China(No.2022XACX0500)。
文摘Understandings of the effect of hot deformation parameters close to the practical production line on grain refinement are crucial for enhancing both the strength and toughness of future rail steels.In this work,the austenite dynamic recrystallization(DRX)behaviors of a eutectoid pearlite rail steel were studied using a thermo-mechanical simulator with hot deformation parameters frequently employed in rail production lines.The single-pass hot deformation results reveal that the prior austenite grain sizes(PAGSs)for samples with different deformation reductions decrease initially with an increase in deformation temperature.However,once the deformation temperature is beyond a certain threshold,the PAGSs start to increase.It can be attributed to the rise in DRX volume fraction and the increase of DRX grain with deformation temperature,respectively.Three-pass hot deformation results show that the accumulated strain generated in the first and second deformation passes can increase the extent of DRX.In the case of complete DRX,PAGS is predominantly determined by the deformation temperature of the final pass.It suggests a strategic approach during industrial production where part of the deformation reduction in low temperature range can be shifted to the medium temperature range to release rolling mill loads.
基金Project supported by the National Natural Science Foundation of China(51590882)the Plan of National Key Research and Development of China(2016YFB0700903)
文摘In this paper,dependence of magnetic properties on microstructure and composition of Ce-Fe-B sintered magnets with Cu-doped Ce-rich alloy addition was investigated.It shows that the maximum energy product(BH)(max)and coercivity H(cj)of Ce-Fe-B sintered magnet are improved from 6.76 to 9.13 MGOe by 35.1%,and from 1.44 to 1.67 kOe by 16.0%,respectively,via adding 5 wt%liquid phase alloy of Ce(35.58)Fe(57.47)Cu6 B(0.95)(at%).Compared with the magnet without Cerich alloy addition,the volume fraction of the grain-boundary phase with low melting point increases in the magnet with Ce-rich alloy additio n,which is be ne ficial to imp roving the microstructure and promoting the coercivity enhancement of the magnet.In the Ce-Fe-B magnet with Ce-rich alloy addition,Cu and Ce enrich in the grain boundaries of the magnet after annealing,therefore the as-annealed magnet has a higher coercivity than the as-sintered magnet.A distinct Fe-rich layer with the average thickness of 60 nm is found in the grain boundaries in the magnet without Ce-rich alloy addition,but it seems that Fe-rich phase disappears in the magnet with Ce-rich alloy addition.The present work suggests that the further improvement of coercivity in the Ce-Fe-B sintered magnets is expectable by designing the composition and structure of added liquid phase alloys.