Strain-Rate Dependency of a Unidirectional Filament Wound Composite under Compression

This article presents the results of experimental studies concerning the dynamic deformation and failure of a unidirectional carbon fiber reinforced plastic(T700/LY113)under compression.The test samples were manufactured through the filament winding of flat plates.To establish the strain rate dependencies of the strength and elastic modulus of the material,dynamic tests were carried out using a drop tower,the Split Hopkinson Pressure Bar method,and standard static tests.The samples were loaded both along and perpendicular to the direction of the reinforcing fiber.The applicability of the obtained samples for static and dynamic tests was confirmed through finite elementmodeling and the high-speed imaging of the deformation and failure of samples during testing.As a result of the conducted experimental studies,static and dynamic stress-strain curves,time dependencies of deformation and the stress and strain rates of the samples during compression were obtained.Based on these results,the strain rate dependencies of the strength and elasticity modulus in the strain rate range of 0.001-6001/s are constructed.It is shown that the strain rate significantly affects the strength and deformation characteristics of the unidirectional carbon fiber composites under compression.An increase in the strain rate by 5 orders of magnitude increased the strength and elastic modulus along the fiber direction by 42%and 50%,respectively.Perpendicular loading resulted in a strength and elastic modulus increase by 58%and 50%,respectively.The average strength along the fibers at the largest studied strain rate was about 1000MPa.The obtained results can be used to design structural elements made of polymer composite materials operating under dynamic shock loads,as well as to build models of mechanical behavior and failure criteria of such materials,taking into account the strain rate effects.

Divergence and flutter instability of magneto-thermo-elastic C-BN hetero-nanotubes conveying fluid

On the basis of finite element analysis,an eigenvalue problem is performed to examine the vibrational characteristics of a hetero-nanotube made of carbon(C)and boron nitride(BN)nanotubes in magnetic and thermal environment.By incorporating the assumption of nonlocal elasticity theory,the size-dependent behavior of the considered structure is also taken into account.The obtained results demonstrate that the onset of the divergence and flutter instabilities may be postponed by exploiting a hetero-nanotube rather than a uniform one composed of carbon nanotube.Moreover,it is exhibited that,in the presence of fluid flow,the mode shape configuration of nanotubes may be different from those of classical modes and therefore the later one should not be utilized in the dynamic analysis of fluid-conveying tubes.Finally,it is shown that,as the temperature decreases,the natural frequencies of the system decrease in high temperature conditions and increase for the case of room temperature.

DYNAMIC PULL-IN INSTABILITY OF DOUBLE-SIDED ACTUATED NANO-TORSIONAL SWITCHES

A nonlinear frequency-amplitude relation is developed to investigate the vibrational amplitude effect on the dynamic pull-in instability of double-sided-actuated nano-torsional switches. The governing equation of a nano-electro-mechanical system pre-deformed by an electric field contains the quintic nonlinear term. The influences of basic parameters on the pull-in instability and natural frequency are investigated using a powerful analytical approach called the homotopy perturbation method. It is demonstrated that two terms in series expansion are sufficient to produce an acceptable solution. The numerical results obtained have verified the soundness of the asymptotic procedure. The phase portraits of the double-sided nano-torsionalactuator exhibit periodic, homoclinic and heteroclinic orbits.