All-solid-state lithium-metal batteries(ASSLMBs)are widely considered as the ultimately advanced lithium batteries owing to their improved energy density and enhanced safety features.Among various solid electrolytes,s...All-solid-state lithium-metal batteries(ASSLMBs)are widely considered as the ultimately advanced lithium batteries owing to their improved energy density and enhanced safety features.Among various solid electrolytes,sulfide solid electrolyte(SSE)Li_(6)PS_(5)Cl has garnered significant attention.However,its application is limited by its poor cyclability and low critical current density(CCD).In this study,we introduce a novel approach to enhance the performance of Li_(6)PS_(5)Cl by doping it with fluorine,using lithium fluoride nanoparticles(LiFs)as the doping precursor.The F-doped electrolyte Li_(6)PS_(5)Cl-0.2LiF(nano)shows a doubled CCD,from 0.5 to 1.0 mA/cm^(2) without compromising the ionic conductivity;in fact,conductivity is enhanced from 2.82 to 3.30 mS/cm,contrary to the typical performance decline seen in conventionally doped Li_(6)PS_(5)Cl electrolytes.In symmetric Li|SSE|Li cells,the lifetime of Li_(6)PS_(5)Cl-0.2LiF(nano)is 4 times longer than that of Li_(6)PS_(5)Cl,achieving 1500 h vs.371 h under a charging/discharging current density of 0.2 mA/cm^(2).In Li|SSE|LiNbO_(3)@NCM721 full cells,which are tested under a cycling rate of 0.1 C at 30℃,the lifetime of Li_(6)PS_(5)Cl-0.2LiF(nano)is four times that of Li_(6)PS_(5)Cl,reaching 100 cycles vs.26 cycles.Therefore,the doping of nano-LiF off ers a promising approach to developing high-performance Li_(6)PS_(5)Cl for ASSLMBs.展开更多
基金supported by the National Key Research and Development Program of China(No.2018YFE0111600)the Haihe Laboratory of Sustainable Chemical Transformations(No.CYZC202307)for financial support。
文摘All-solid-state lithium-metal batteries(ASSLMBs)are widely considered as the ultimately advanced lithium batteries owing to their improved energy density and enhanced safety features.Among various solid electrolytes,sulfide solid electrolyte(SSE)Li_(6)PS_(5)Cl has garnered significant attention.However,its application is limited by its poor cyclability and low critical current density(CCD).In this study,we introduce a novel approach to enhance the performance of Li_(6)PS_(5)Cl by doping it with fluorine,using lithium fluoride nanoparticles(LiFs)as the doping precursor.The F-doped electrolyte Li_(6)PS_(5)Cl-0.2LiF(nano)shows a doubled CCD,from 0.5 to 1.0 mA/cm^(2) without compromising the ionic conductivity;in fact,conductivity is enhanced from 2.82 to 3.30 mS/cm,contrary to the typical performance decline seen in conventionally doped Li_(6)PS_(5)Cl electrolytes.In symmetric Li|SSE|Li cells,the lifetime of Li_(6)PS_(5)Cl-0.2LiF(nano)is 4 times longer than that of Li_(6)PS_(5)Cl,achieving 1500 h vs.371 h under a charging/discharging current density of 0.2 mA/cm^(2).In Li|SSE|LiNbO_(3)@NCM721 full cells,which are tested under a cycling rate of 0.1 C at 30℃,the lifetime of Li_(6)PS_(5)Cl-0.2LiF(nano)is four times that of Li_(6)PS_(5)Cl,reaching 100 cycles vs.26 cycles.Therefore,the doping of nano-LiF off ers a promising approach to developing high-performance Li_(6)PS_(5)Cl for ASSLMBs.