in order to improve the optical and mechanical performances of waterborne polyurethane （WPU）, nanocrystalline cellulose （NCC）/WPU composites were synthesized in this study. NCC （prepared by acid hydrolysis of cot...in order to improve the optical and mechanical performances of waterborne polyurethane （WPU）, nanocrystalline cellulose （NCC）/WPU composites were synthesized in this study. NCC （prepared by acid hydrolysis of cotton fiber） was modified by （3-aminopropyl）triethoxysilane （APTES） to enhance its compatibility with WPU, and the surface-modified NCC was characterized by grafting ratio, crystallinity and contact angle （CA）. NCC/WPU composites were examined by scanning electron microscopy （SEM）, X-ray powder diffraction （XRD） and thermogravimetric analysis （TG）. The anti-yellowing property, specular gloss, pencil hardness, and abrasion resistance of NCC/WPU composites were investigated by the methods of Chinese National Standards GB/T 23999-2009, GB/T 9754-2007, GB/T 6739-2006 and GB/T 1768-2006, respectively. The results showed that the grafting ratio of NCC modified by 6% APTES was 36.01% and the crystallinity of modified NCC was decreased with the enhancement of APTES. CA of the modified NCC was decreased by 28.8% and the nanoparticles were homogeneously dispersed in the WPU matrix. The XRD patterns of the NCC/WPU composites were relatively steady, while the thermal stability of the composites was enhanced by 6.7% with 1.0 wt% modified NCC. Modified NCC affected the specular gloss of NCC/WPU composites more obviously than the anti-yellowing property. The pencil hardness of NCC/WPU composites was increased from 2H to 4H by addition of NCC and the abrasion resistance of the composites was enhanced significantly. In general, NCC/WPU composites showed significant improvements in the optical and mechanical performances.展开更多
基金financially supported by the"Fundamental Research Funds for the Central Universities"(No.BLYJ201301)the Forestry Industry Research Special Funds for Public Welfare Projects:Research and Demonstration of Fast-growing Wood Modification and Application(201204702-B2)
文摘in order to improve the optical and mechanical performances of waterborne polyurethane （WPU）, nanocrystalline cellulose （NCC）/WPU composites were synthesized in this study. NCC （prepared by acid hydrolysis of cotton fiber） was modified by （3-aminopropyl）triethoxysilane （APTES） to enhance its compatibility with WPU, and the surface-modified NCC was characterized by grafting ratio, crystallinity and contact angle （CA）. NCC/WPU composites were examined by scanning electron microscopy （SEM）, X-ray powder diffraction （XRD） and thermogravimetric analysis （TG）. The anti-yellowing property, specular gloss, pencil hardness, and abrasion resistance of NCC/WPU composites were investigated by the methods of Chinese National Standards GB/T 23999-2009, GB/T 9754-2007, GB/T 6739-2006 and GB/T 1768-2006, respectively. The results showed that the grafting ratio of NCC modified by 6% APTES was 36.01% and the crystallinity of modified NCC was decreased with the enhancement of APTES. CA of the modified NCC was decreased by 28.8% and the nanoparticles were homogeneously dispersed in the WPU matrix. The XRD patterns of the NCC/WPU composites were relatively steady, while the thermal stability of the composites was enhanced by 6.7% with 1.0 wt% modified NCC. Modified NCC affected the specular gloss of NCC/WPU composites more obviously than the anti-yellowing property. The pencil hardness of NCC/WPU composites was increased from 2H to 4H by addition of NCC and the abrasion resistance of the composites was enhanced significantly. In general, NCC/WPU composites showed significant improvements in the optical and mechanical performances.
