The solidification behavior, micro structure and silicon twinning of Al-10 Si alloys with Yb addition were investigated by thermal analysis, optical microscopy, X-ray diffraction. scanning electron microscopy, and tra...The solidification behavior, micro structure and silicon twinning of Al-10 Si alloys with Yb addition were investigated by thermal analysis, optical microscopy, X-ray diffraction. scanning electron microscopy, and transmission electron microscopy. The results indicate that the nucleation temperature, minimum temperature, and growth temperature of Al-lOSi alloys decrease with increasing Yb content. The cooling curves of the Yb-modified alloys exhibit marked recalescence. The recalescence of the modified alloy peaks at 2.3 ℃ when the Yb content is 0.7 wt%. The 3 D morphologies of eutectic Si in Yb-modified alloys change from a coarse plate-like structure to a honeycomb structure with many fine fibrous structures.The Al-Si-Yb intermetallic compound is observed in the 1.0 wt% Yb-modified alloy. Meanwhile, XRD analysis and TEM results indicate that the average twin spacing in the Yb-modified alloys is 18-46.2 nm.The average twin spacing of eutectic Si decreases with increasing Yb content. When the Yb content in the modified alloy is increased to 0.7 wt%, the average twin spacing value of eutectic Si reaches to 18 nm,which promotes the formation of twins and refinement of eutectic Si.展开更多
基金supported by the National Natural Science Foundation of China(51405216)the Training Programme Foundation for Young Scientists of Jiangxi Province(20153BCB23023)the Natural Science Foundation of Jiangxi Province(20171BAB206005)
文摘The solidification behavior, micro structure and silicon twinning of Al-10 Si alloys with Yb addition were investigated by thermal analysis, optical microscopy, X-ray diffraction. scanning electron microscopy, and transmission electron microscopy. The results indicate that the nucleation temperature, minimum temperature, and growth temperature of Al-lOSi alloys decrease with increasing Yb content. The cooling curves of the Yb-modified alloys exhibit marked recalescence. The recalescence of the modified alloy peaks at 2.3 ℃ when the Yb content is 0.7 wt%. The 3 D morphologies of eutectic Si in Yb-modified alloys change from a coarse plate-like structure to a honeycomb structure with many fine fibrous structures.The Al-Si-Yb intermetallic compound is observed in the 1.0 wt% Yb-modified alloy. Meanwhile, XRD analysis and TEM results indicate that the average twin spacing in the Yb-modified alloys is 18-46.2 nm.The average twin spacing of eutectic Si decreases with increasing Yb content. When the Yb content in the modified alloy is increased to 0.7 wt%, the average twin spacing value of eutectic Si reaches to 18 nm,which promotes the formation of twins and refinement of eutectic Si.