La_((1-x))Mg_xNi_(4.25)Al_(0.75)(x = 0.0, 0.1, 0.2, 0.3)alloys for tritium storage were prepared by a method of electromagnetic induction melting. The crystal structure and hydrogen storage performance of the as-cast ...La_((1-x))Mg_xNi_(4.25)Al_(0.75)(x = 0.0, 0.1, 0.2, 0.3)alloys for tritium storage were prepared by a method of electromagnetic induction melting. The crystal structure and hydrogen storage performance of the as-cast alloys were investigated. The results showed that a single phase of La Ni_4Al was in the alloys with x = 0.0 and 0.1 and that LaNi_4Al and second phase of(La,Mg)Ni)_3 and AlNi_3 were in the alloys with x = 0.2 and 0.3. On the other hand, the plateau pressures of P–C isotherms of the alloys were increased with the rise of the x value from 0.2 to 0.3 and the hydrogen storage capacity was obviously degraded simultaneously. It was found that the alloy had faster absorption kinetics as the proportion of Mg increased from 0.1 to 0.3.展开更多
基金supported by the Strategic Priority Research Program of the Chinese Academy of Sciences (XDA02020200)the National Natural Science Foundation of China (No. 11475145)the Yangzhou Foundation for Development of Science and Technology (No. YZ2014041)
文摘La_((1-x))Mg_xNi_(4.25)Al_(0.75)(x = 0.0, 0.1, 0.2, 0.3)alloys for tritium storage were prepared by a method of electromagnetic induction melting. The crystal structure and hydrogen storage performance of the as-cast alloys were investigated. The results showed that a single phase of La Ni_4Al was in the alloys with x = 0.0 and 0.1 and that LaNi_4Al and second phase of(La,Mg)Ni)_3 and AlNi_3 were in the alloys with x = 0.2 and 0.3. On the other hand, the plateau pressures of P–C isotherms of the alloys were increased with the rise of the x value from 0.2 to 0.3 and the hydrogen storage capacity was obviously degraded simultaneously. It was found that the alloy had faster absorption kinetics as the proportion of Mg increased from 0.1 to 0.3.