Tensile properties and fracture reliability of a glass-coated Co-based amorphous microwire

Co68.15Fe4.35Si12.25B15.25 （at%） amorphous microwires with a smooth surface and a circular cross-section were fabricated by the glass-coated melt spinning method. Their mechanical properties were evaluated through tensile tests of the glass-coated amorphous mi-crowires, and their fracture reliability was estimated using two-and three-parameter Weibull analysis. X-ray diffraction and transmission electron microscopy results showed that these glass-coated Co-based microwires were mostly amorphous. The coated Co-based microwires exhibit a tensile strength of 1145 to 2457 MPa, with a mean value of 1727 MPa and a variance of 445 MPa. Weibull statistical analysis showed that the tensile two-parameter Weibull modulus of the amorphous microwires is 4.16 and the three-parameter Weibull modulus is 1.61 with a threshold value as high as 942 MPa. These results indicate that the fabricated microwires exhibit good tensile properties and fracture reliability, and thus appear to be good candidates for electronics reliability engineering applications.

Impacts of zinc layer and pouring method on interface performance for Al-22Si/ZL104 bi-metal

Bi-metal material consisting of spray-formed Al-22Si and ZL104 is a suitable candidate for applications in internal combustion engines. This research investigated the effects of surface treatment and appropriate gating system on the microstructures and mechanical properties in evaluating the optimal strategy for producing high quality bi-metal materials. The bi-metal materials were prepared using ZL104 gravity casting by different pouring types around the spray-formed AI-22Si with varied surface treatments. The wettability between AI-22Si and ZL104 was significantly improved when Zn coating was used to remove the natural oxide layer. This research also obtained the improved interfacial microstructures and interracial bonding strength for materials when applying the appropriate pouring method. The hardness profiles of AI-22Si/ZL104 bi-metal were consistent with the observed microstructures. The average tensile strength of the bi-metal material with zinc coating is -42.3 MPa, which is much higher than that with oxide film at -10 MPa. The process presented is a promising and effective approach for developing materials in the automotive industry.

Microstructure and magnetocaloric properties of melt-extracted SmGdDyCoAl high-entropy amorphous microwires

This paper presents a systematic investigation of the microstructure and magnetocaloric properties of melt-extracted Sm_(20)Gd_(20)Dy_(20)Co_(20)Al_(20)high-entropy microwires.The fabricated wires exhibited an amorphous structure,and the temperature interval of the undercooled liquid AT was 45 K.The microwires underwent a second-order magnetic transition from a ferromagnetic to a paramagnetic state near the Curie temperature(T_(C)=52 K),The maximum magnetic entropy change(-ΔS_M^(max)),the relative cooling power and the refrigeration capacity reached 6.34 J·kg^(-1)·K^(-1).422.09 J·kg^(-1)and 332.94 J·kg^(-1),respectively,under a magnetic field change of 5 T.In addition,the temperature-averaged entropy changes with two temperature lifts(3 and 10 K)were 6.32 and 6.27 J·kg^(-1)·K^(-1),respectively.The good magnetocalorie performance highlights the significant potential for the Sm_(20)Gd_(20)Dy_(20)Co_(20)Al_(20)microwires to be used as magnetic refrigerant materials in low-temperature region applications.This work will serve as a valuable reference for future investigations on low-temperature high-entropy magnetocaloric materials.

Effect of Al22Si/ZL102 bimetal interface fabricated by extrusion at neareutectic temperature

The Al22Si/ZL102 bimetal was designed and prepared by extrusion at near-eutectic temperature.The properties and fracture behaviors of different surface treatments between oxide film and zinc coating were compared between the Al22 Si and ZL102 bimetal.The average bonding strength of bimetal with intermittent oxide film interface was about 89.3MPa,which is higher than that of the bimetal fabricated by zinc coating method（about 76.3MPa）.During the process of extrusion,the oxidation film was extruded to crush and the metal was extruded through the micro-cracks of the oxidation film,then the two surfaces were joined together.Altogether,the results showed that extrusion at near-eutectic temperature is favorable for achieving a high-quality metallurgical bonded interface.

Mechanical property statistical analysis of Gd50Al30Co20 amorphous wires for providing reference to design requirements of cooling system

Gd50Al3oCo20 wires show excellent magnetocaloric properties and high heat exchange rate due to the microsize. The Weibull and lognormal methods were used for systematically analyzing its mechanical properties for matching the design requirements in cooling system. The wire exhibits average fracture strength of-969.5 MPa and typical fracture behavior of amorphous character. Moreover, the distributions of stresses for tensile strains at 10 values are estimated by probability plot and Chi-square goodness-of-fit test. The random stresses were best fitted by lognormal probability distribution for most studied cases; however, fracture strength was best fitted by Weibull probability distribution. It is interesting to note that the mean and standard deviation of the stresses （to reach specific tensile strain） increase as the tensile strain grows, accompanied by the coefficients of variation of stresses which decrease smoothly. It is concluded that the inhomogeneity of material does cause the scatter of stresses growth, and the scatter could be considerably large.