Microstructure and mechanical properties of friction stir processed Al−Mg2Si alloys 被引量:2
1
作者 Qing-dong QIN hong-long zhao +2 位作者 Juan LI Ying-zhe ZHANG Xiang-dong SU 《Transactions of Nonferrous Metals Society of China》 SCIE EI CAS CSCD 2020年第9期2355-2368,共14页
The microstructure and mechanical properties of friction stir processed Al−Mg2Si alloys were studied by TEM and EBSD.The results showed that an increase in the tool rotation speed(300−700 r/min)led to a decrease in th... The microstructure and mechanical properties of friction stir processed Al−Mg2Si alloys were studied by TEM and EBSD.The results showed that an increase in the tool rotation speed(300−700 r/min)led to a decrease in the defect area(from 10.5 mm2 to zero),whereas the defect area demonstrated the opposite trend(increased to 1.5 mm2 from zero)upon further increasing the rotation speed(700−1200 r/min).The types of defects were transformed from tunnel defects to fusion defects as the rotational speed increased.The coarse Mg2Si dendrites were broken and fine particles(smaller than 10mm)formed in the weld nugget(WN).The amount of low-angle grain boundaries increased significantly from 57.7%to 83.6%,which was caused by an increase in the content of the deformed structure(from 1.7%to 13.6%).The hardness,ultimate tensile strength(UTS)and elongation were all greatly improved for the weld nugget.The hardness values of the WNs had the following order:R300<R1200<R500<R900<R700.The UTS and elongation had the following order:BM(base material)<R300<R1200<R500<R900<R700.The UTS and the elongation for the WN were increased by one and three times,respectively. 展开更多
关键词 Al−Mg2Si alloy friction stir processing ultimate tensile strength microstructural evolution DEFECT
下载PDF
上一页 1 下一页 到第
使用帮助 返回顶部