To fabricate W-ZrC composite through reaction sintering at first WC and ZrO2 powders with molar ratio of 3-1 are ball milled, then the green body made from this mixture is sintered. Since reactivity is the main proble...To fabricate W-ZrC composite through reaction sintering at first WC and ZrO2 powders with molar ratio of 3-1 are ball milled, then the green body made from this mixture is sintered. Since reactivity is the main problem in sintering of mironized powders the starting ZrO2 powder is selected in nano size to see whether the reaction improves. The XRD pattern indicates that W-ZrC composite has been formed, although some unreacted compounds still exist and some unwanted components have been created. In the case of using nano powders the amount of unreacted WC and ZrO2 phases and unwanted W2C phase reduces and the reaction progresses better. Additionally by using nano powders the reaction progressed and the mechanical proprieties including density, hardness, Elastic modulus and Flexural strength improved.展开更多
文摘To fabricate W-ZrC composite through reaction sintering at first WC and ZrO2 powders with molar ratio of 3-1 are ball milled, then the green body made from this mixture is sintered. Since reactivity is the main problem in sintering of mironized powders the starting ZrO2 powder is selected in nano size to see whether the reaction improves. The XRD pattern indicates that W-ZrC composite has been formed, although some unreacted compounds still exist and some unwanted components have been created. In the case of using nano powders the amount of unreacted WC and ZrO2 phases and unwanted W2C phase reduces and the reaction progresses better. Additionally by using nano powders the reaction progressed and the mechanical proprieties including density, hardness, Elastic modulus and Flexural strength improved.